Abstract:Various alumina particles were investigated for use as core reinforcement to strengthen aluminous-porcelain jacket crowns. The alumina particles were either spherical or nonspherical and were between 5.3 microns and 60 microns in size. Initially comparisons were made among such properties as particle-size distribution, apparent density, specific surface area, and flow. Then each alumina powder was mixed with feldspar at rates of from 10wt% to 70wt% at increments of 10wt%. Formed into columns, the powder was fired at 1350 degrees C for 5 minutes. The resulting feldspar-alumina composites were compared for shrinkage then cut and prepared into disc specimens. The disc-rupture test was employed to measure composite strengths. A scanning electron microscope was employed to observe alumina particles and composite cross sections. Results 1. Spherical alumina (average particle size 5.4 microns), spherical alumina (average particle size 28.9 microns), and nonspherical alumina (average particle size 58.0 microns) were higher in apparent density and flow rate but lower in specific surface area. 2. Feldspar-alumina composites shrank approximately 30%; shrinkage of 15-20% occurred only in composites involving spherical alumina (average particle size 5.4 microns). 3. Composites of feldspar and spherical alumina were observed to be stronger than those of feldspar and nonspherical alumina. Composites containing 50-60wt% (especially when the alumina particle size was 5.4 microns) were the sturdiest. 4. Increasing the amount of alumina proportionally increased composite strength. In composites containing nonspherical alumina, volume amount and strength were not always proportional. 5. Microscopic examination of composite cross sections showed uniform dispersion of spherical alumina but no dispersion of nonspherical alumina. In conclusion, spherical alumina (especially when average particle size is 5.4 microns) demonstrated the best powder properties as a reinforcing core material and therefore is most suitable for reinforcing the core of the porcelain jacket crown.

Influence of Different Particle Gradation of Corundum on Performance of Porous Alumina-based Ceramic Cores

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Fabrication of porous alumina-based ceramic core using aluminium as pore-forming agent

Effect of Particle Size on Properties of Alumina-Based Ceramic Cores

Influence of Al2O3 Fiber on the Properties Al2O3-Based Ceramic Core

Effect Of Zirconia Content And Particle Size On The Properties Of 3d-Printed Alumina-Based Ceramic Cores

Effect of Core-Shell Microspheres As Pore-Forming Agent on the Properties of Porous Alumina Ceramics

Effect Of Silica Sol On The Properties Of Alumina-Based Duplex Ceramic Cores

The Effect of Different Minerals on the Property of Alumina Ceramic Cores

Alumina-Based Ceramic Core Nano-Composites For Investment Casting

Influences of Composition of Starting Powders and Sintering Temperature on the Pore Size Distribution of Porous Corundum-Mullite Ceramics

[Reinforcement of cores on porcelain jacket crowns. Influence of alumina powder properties on the cores]

Particle size gradation design and performance enhancement of quartz cores for precision casting

Effects of sintering temperature on pore characterization and strength of porous corundum-mullite ceramics

The Study on Properties of Soluble Alumina Based Ceramic Cores

Fabrication and properties of porous alumina ceramics with three different pore sizes

Influence of powder particle size on microstructure and performance of calcium oxide based ceramic core

Effect of Silicone Resin Content on the Properties of Al2O3-Based Ceramic Cores

The influence of sintering procedure and porosity on the properties of 3D printed alumina ceramic cores

Effect of Yttrium Aluminum Garnet on High-Temperature Properties of Alumina-Based Ceramic Cores

Silica-Based Ceramic Core For Aviation Applications: Facile Pore Filling And Flexural Strength Improvement