Abstract:In this work, the effects of porosity and different particle sizes of pore‐forming agent on the mechanical properties of porous alumina ceramics have been reported. Different grades of porous alumina ceramics were developed using corn cob (CC) of different weight contents (5, 10, 15 and 20 wt%) and particle sizes (<63 µm, 63‐125 µm and 125‐250 µm) as the pore‐forming agent. Experimental results showed thattotal porosity and pore cavity size of the porous alumina ceramics increased with rising addition of CC pore former. Total porosity increased with increasing particle size of CC with the Al2O3‐<63CC5 sample exhibiting the lowest total porosity of 41.3 vol% while the highest total porosity of 68.1 vol% was exhibited by the Al2O3‐125‐250CC20. The particle size effect of CC on the mechanical properties revealed that diametral tensile strength and hardness of the porous alumina ceramics deteriorated with increasing particle size of CC pore former. The Al2O3‐<63CC5 sample exhibited the highest diametral tensile strength and hardness of 25.1 MPa and 768.2 HV respectively, while Al2O3‐125‐250CC20 exhibited the lowest values of 1.1 MPa and 35.9 HV. Overall, porous alumina ceramics with the smallest pore sizes under each particle size category exhibited superior mechanical properties in their respective categories.

Tailored pore structures and mechanical properties of porous alumina ceramics prepared with corn cob pore‐forming agent

Effect of Type and Content of Pore-forming Agents on Properties of Porous Alumina Membrane Support

Fabrication and properties of porous alumina ceramics with three different pore sizes

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Effects of pore structure on thermal conductivity and strength of alumina porous ceramics using carbon black as pore-forming agent

Preparation and properties of porous alumina ceramics with oriented cylindrical pores produced by an extrusion method

The effect of nano-copper additives on the porosity, mechanical properties, and microstructure of alumina ceramics using commercial rice husk ash as a pore former

Microstructure and Mechanical Properties of Porous Alumina Ceramics Fabricated by the Decomposition of Aluminum Hydroxide

Preparation and properties of porous alumina with highly ordered and unidirectional oriented pores by a self-organization process

Rice Husk as a Pore-Forming Agent: Impact of Particle Size on the Porosity and Diametral Tensile Strength of Porous Alumina Ceramics

Enhanced mechanical properties and decreased thermal conductivity of porous alumina ceramics by optimizing pore structure

Gas permeability and mechanical properties of porous alumina ceramics with unidirectionally aligned pores

Effect of Alumina Fiber Content on Pore Structure and Properties of Porous Ceramics

Alumina Porous Ceramics Obtained by Freeze Casting: Structure and Mechanical Behaviour under Compression

Microstructure and mechanical and thermal shock properties of hierarchically porous ceramics

Preparation of porous alumina abrasives and their chemical mechanical polishing behavior

Al2O3 Ceramics with Well-Oriented and Hexagonally Ordered Pores: the Formation of Microstructures and the Control of Properties

A Novel Approach to Fabricate Porous Alumina Ceramics with Excellent Properties Via Pore-Forming Agent Combined with Sol Impregnation Technique

Effect of pore structure evolution on mechanical properties and thermal conductivity of porous SiC-Mullite ceramics

Alumina ceramics prepared with new pore-forming agents

Preparation and properties of porous alumina ceramics for ultra-precision aerostatic bearings