Abstract:Air bearing has been widely applied in ultra-precision machine tools, aerospace and other fields. The restrictor of the porous material is the key component in air bearings, but its performance is limited by the machining accuracy. A combination of optimization design and material modification of the porous alumina ceramic membrane is proposed to improve performance within an air bearing. Porous alumina ceramics were prepared by adding a pore-forming agent and performing solid-phase sintering at 1600 °C for 3 h, using 95-Al2O3 as raw material and polystyrene microspheres with different particle sizes as the pore-forming agent. With 20 wt.% of PS50, the optimum porous alumina ceramic membranes achieved a density of 3.2 g/cm3, a porosity of 11.8% and a bending strength of 150.4 MPa. Then, the sintered samples were processed into restrictors with a diameter of 40 mm and a thickness of 5 mm. After the restrictors were bonded to aluminum shells for the air bearing, both experimental and simulation work was carried out to verify the designed air bearing. Simulation results showed that the load capacity increased from 94 N to 523 N when the porosity increased from 5% to 25% at a fixed gas supply pressure of 0.5 MPa and a fixed gas film thickness of 25 μm. When the gas film thickness and porosity were fixed at 100 μm and 11.8%, respectively, the load capacity increased from 8.6 N to 40.8 N with the gas supply pressure having been increased from 0.1 MPa to 0.5 MPa. Both experimental and simulation results successfully demonstrated the stability and effectiveness of the proposed method. The porosity is an important factor for improving the performance of an air bearing, and it can be optimized to enhance the bearing’s stability and load capacity.

Preparation and properties of porous alumina ceramics for ultra-precision aerostatic bearings

Rational Design and Porosity of Porous Alumina Ceramic Membrane for Air Bearing

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Effect of Type and Content of Pore-forming Agents on Properties of Porous Alumina Membrane Support

Fabrication and properties of porous alumina ceramics with three different pore sizes

Preparation and properties of porous alumina with highly ordered and unidirectional oriented pores by a self-organization process

Air permeable alumina-based porous ceramics with high performance prepared by novel gel casting route

High-strength porous alumina ceramics prepared from stable wet foams

Preparation of porous alumina ceramic with ultra-high porosity and long straight pores by freeze casting

Gas permeability and mechanical properties of porous alumina ceramics with unidirectionally aligned pores

Design and Formulation of Polyurethane Foam Used for Porous Alumina Ceramics

Preparation of Self-Lubricating Porous Alumina Ceramics with PMMA /PAO6 Microcapsules and Their Tribological Properties

Enhanced mechanical properties and decreased thermal conductivity of porous alumina ceramics by optimizing pore structure

Tailored pore structures and mechanical properties of porous alumina ceramics prepared with corn cob pore‐forming agent

Preparation of porous alumina abrasives and their chemical mechanical polishing behavior

Microstructure and Properties of Alumina Ceramics Prepared from Submicrometer Alumina Powder with MgO–ZrO2 Coated on Alumina Grain Surface

Preparation and properties of porous alumina ceramics with oriented cylindrical pores produced by an extrusion method

High-precision and Rapid Layerless Printing Technology for High-Solid and Low-Viscosity Alumina Slurry

Preparation and research of fine-grained alumina with high mechanical properties

Ultrahigh‐strength Alumina Ceramic Foams Via Gelation of Foamed Boehmite Sol

Ultra-high Porosity of Open-Cell Alumina Ceramic Foams Prepared by Adding Tiny Amounts of Γ-Alo(oh) Sol