Abstract:In this paper, an optimized process for preparation of photosensitive nanosilica from rice husk (RH) is described. The rice husk sample was pretreated by soaking in deionized water to remove most of the alkali metals and partial fixed carbon. Most metal oxides, especially alkaline metal oxides and alkaline-earth metal oxides, were removed to a certain extent after the soaking pre-treatment. Soaking pretreatment may remove the hydrogen bonds or extractives between hemi-cellulose and cellulose, which affects the thermal stability of both molecules. To thoroughly analyze the soaking process, thermogravimetric analysis (TGA) was performed to obtain the mass loss behavior of soaked rice husk. The characteristics of the nanosilica prepared from the method described in this paper are superior to those of fumed silica. The silica content of the nanosilica reached a record of 99.92% in pyrolysis method. The optimum preparation conditions were as follows: a rice husk feedstock particle size of between 250 and 420 mu m, a pyrolysis temperature of approximately 610 degrees C, a hydrolysis temperature of 120 degrees C, a 1:10 (g/ml) ratio of rice husk to acid, a hydrolysis time of 4 h, and a hydrochloric acid (HCI) concentration of 8% (wt.%). A detailed study of the effects of the pyrolysis temperature and feedstock particle size was conducted, filling the gap in systematic research on the nanosilica preparation process using the pyrolysis method. The complete process of pyrolysis for pretreated rice husk is described, including the decomposition of the major constituents, volatilization of gases and the formation of silica. The results of this study provide a deep understanding of nanosilica production by pyrolyzation. The prepared nanosilica is photosensitive and approximately spheroidal with an average particle size of approximately 8-10 nm. (C) 2013 Elsevier B.V. All rights reserved.

Rice Husk as a Pore-Forming Agent: Impact of Particle Size on the Porosity and Diametral Tensile Strength of Porous Alumina Ceramics

Effect of Type and Content of Pore-forming Agents on Properties of Porous Alumina Membrane Support

Preparation of Fly Ash-Based Porous Ceramic with Alumina as the Pore-Forming Agent

Tailored pore structures and mechanical properties of porous alumina ceramics prepared with corn cob pore‐forming agent

Fabrication Of Sio2 Porous Ceramics From Rice Husk Ash

The effect of nano-copper additives on the porosity, mechanical properties, and microstructure of alumina ceramics using commercial rice husk ash as a pore former

Fabrication of SiO<sub>2</sub> Porous Ceramics from Rice Husk Ash

Rice Husk Ash as Pore Former and Reinforcement on the Porosity, Microstructure, and Tensile Strength of Aluminum MMC Fabricated via the Powder Metallurgy Method

INFLUENCE OF Al2O3 ON PREPARING POROUS SILICON NITRIDE BASED CERAMIC FROM RICE HUSK

Processing and Characterization of Nano Silica and Iron Oxide Coated Silica Composites Extracted from Rice Hulls

Novel design of elongated mullite reinforced highly porous alumina ceramics using carbonized rice husk as pore-forming agent

Improvement of the characteristics of silica particles extracted from rice husks using chemical-physical method

Conversion of rice husks into carbonaceous materials with porous structures via hydrothermal process

Mesoporous Silica with an Alveolar Construction Obtained by Eco-Friendly Treatment of Rice Husks

A Detailed Study of the Effects of Pyrolysis Temperature and Feedstock Particle Size on the Preparation of Nanosilica from Rice Husk

Recycling bagasse and rice hulls ash as a pore‐forming agent in the fabrication of cordierite‐spinel porous ceramics

review of rice husk silica as a heterogeneous catalyst support

Effect of the Zirconia Particle Size on the Compressive Strength of Reticulated Porous Zirconia-Toughened Alumina

Influence of pre-treatment processes on the purity and characteristics of silica extracted from rice husk

Effect of Alumina Fiber Content on Pore Structure and Properties of Porous Ceramics

Effects of Alkali/Char Ratio and Activation Temperature on Ultramicropores of Rice Husk Active Carbon