Abstract:Spinel oxides with the general formula of MnCuxCo2−xO4 (x = 0.1, 0.3, 0.5, 0.7 respectively) are used as coating materials on the metallic interconnect SUS 430 alloy to reduce the cathodic performance degradation by Cr poisoning and the interfacial resistance to improve the surface stability. The effect of Cu doping at the B position of spinel on the electrical conductivity and coefficient of temperature expansion (CTE) is investigated to determine the oxidation behavior and effectiveness as a protective layer. The result confirms that MnCu0.5Co1.5O4 spinel shows highest electrical conductivity of 105.46 S cm−1 at 750 °C in air and an average CTE value of 12.27 × 10−6 K−1 at temperature range of 20–960 °C. MnCu0.5Co1.5O4 coating is stable enough after 2000 h cyclic oxidation at 750 °C. The growth of Cr2O3 and formation of MnCr2O4 in the scale layer are effectively suppressed by the presence of MnCu0.5Co1.5O4 coating. The oxidation kinetics obeys the parabolic law with a rate constant as low as 2.76 × 10−15 g2 cm−4·s−1 and the ASR contributed by the oxide scale is 8.04 mΩ cm2 at 750 °C. The research indicates that MnCu0.5Co1.5O4 is a promising coating material for metallic interconnects of the intermediate temperature solid oxide fuel cells.

High-temperature oxidation process analysis of MnCo2O4 coating on Fe–21Cr alloy

Experimental Investigation of the Initial Stage of the Oxidation Mechanism of Co Coating for Solid Oxide Fuel Cell Interconnects at 650 °C

Oxidation behavior of Cu-doped MnCo 2 O 4 spinel coating on ferritic stainless steels for solid oxide fuel cell interconnects

High-entropy FeCoNiMnCu alloy coating on ferritic stainless steel for solid oxide fuel cell interconnects

Mn 1.4 Co 1.4 Cu 0.2 O 4 spinel protective coating on ferritic stainless steels for solid oxide fuel cell interconnect applications

Cyclic oxidation of Mn–Co spinel coated SUS 430 alloy in the cathodic atmosphere of solid oxide fuel cells

High temperature oxidation and chromium volatilisation of AISI 430 stainless steel coated by Mn-Co and Mn-Co-Cu oxides for SOFC interconnect application

Effect of bias voltage on high-temperature oxidation resistance and electrical properties of Mn-Co coating with metal interconnects for solid oxide fuel cell

Oxidation Behavior of Ferritic Stainless Steel Interconnect Coated by a Simple Diffusion Bonded Cobalt Protective Layer for Solid Oxide Fuel Cells

Cu-Fe spinel coating as oxidation barrier for Fe-16Cr metallic interconnect in solid oxide fuel cells

Cu doped Mn-Co spinel protective coating on ferritic stainless steels for SOFC interconnect applications

Fabricating a MnCo coating to improve oxidation resistance and electrical conductivity of Crofer22H alloy as SOFC interconnect

Comparison of iron and copper doped manganese cobalt spinel oxides as protective coatings for solid oxide fuel cell interconnects

The Preparation and Properties of Ti(Nb)-Si-C Coating on the Pre-Oxidized Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

Research on Fabrication and Property of NiMn2 O4 Coatings for Fe-Cr Alloy Interconnect Applications

Thermal Growth and Performance of Manganese Cobaltite Spinel Protection Layers on Ferritic Stainless Steel SOFC Interconnects

Ni–Co/ZrO2 Composite Coatings via Electroless Plating on Crofer 22APU for SOFC Interconnect Applications: Oxidation and Chromium Vaporization Behavior

CrxN/Mn1.7Cu1.3 coating on ferritic stainless steel for solid oxide fuel cell interconnects

The electrical property of MnCo2O4 and its application for SUS 430 metallic interconnect

Supersonic spray derived Cu–Co oxide coating on SUS441 to protect the metallic interconnect and to increase stability of SOFC cathode

Oxidation Kinetics and Phase Evolution of a Fe–16Cr Alloy in Simulated SOFC Cathode Atmosphere