Abstract:AISI 430 stainless steel is used for interconnects in solid oxide fuel cells (SOFCs). One of the main problems with this steel is the formation of chromia scales during oxidation at high temperature and thus increasing electrical resistance. In order to solve such problems, a protective and conductive coating layer can be applied on interconnects. In this study, AISI 430 steel was coated by Ni–P–TiO2–ZrO2 composite coating. To evaluate the oxidation behavior, isothermal and cyclic oxidation tests were used at 800 °C. Area specific resistances (ASR) of uncoated and coated samples were also compared as a function of time during oxidation at 800 °C. Chemical composition and surface morphology of the samples were examined before and after oxidation by Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD). In isothermal and cyclic oxidation tests, coated samples showed lower weight gain due to the formation of Ni2P2O7, Ni3P2O8, and NiFe2O4 spinel. This spinel prevented outward Cr diffusion, and improved the oxidation resistance of the AISI 430 stainless steel substrate. The obtained result by cyclic oxidation revealed that the coated substrates were resistant against cracking and spallation. Also, the results showed that the formation of Ni2P2O7, Ni3P2O8, and NiFe2O4 spinel and also the presence of TiO2 and ZrO2 caused ASR reduction. ASR of Ni–P–TiO2–ZrO2-coated specimens after 300 h of oxidation at 800 ºC (14.21 mΩ cm2) was lower than the uncoated specimens (41.84 mΩ m2) after the same time of oxidation.

Oxidation Behavior of Ferritic Stainless Steel Interconnect Coated by a Simple Diffusion Bonded Cobalt Protective Layer for Solid Oxide Fuel Cells

The Preparation and Properties of Ti(Nb)-Si-C Coating on the Pre-Oxidized Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

Experimental Investigation of the Initial Stage of the Oxidation Mechanism of Co Coating for Solid Oxide Fuel Cell Interconnects at 650 °C

High-entropy FeCoNiMnCu alloy coating on ferritic stainless steel for solid oxide fuel cell interconnects

CrxN/Mn1.7Cu1.3 coating on ferritic stainless steel for solid oxide fuel cell interconnects

The effect of surface treatment on the oxidation of ferritic stainless steels used for solid oxide fuel cell interconnects

Oxidation and electrical behavior of AISI 430 steel coated with Ni–P–TiO2–ZrO2 composite for SOFC interconnect application

The Effect of Metallic Co-Coating Thickness on Ferritic Stainless Steels Intended for Use as Interconnect Material in Intermediate Temperature Solid Oxide Fuel Cells

Supersonic spray derived Cu–Co oxide coating on SUS441 to protect the metallic interconnect and to increase stability of SOFC cathode

Protective/Conductive Coatings on Ferritic Stainless Steels for Solid Oxide Fuel Cell Interconnect Applications

Ni–Co/ZrO2 Composite Coatings via Electroless Plating on Crofer 22APU for SOFC Interconnect Applications: Oxidation and Chromium Vaporization Behavior

Cu doped Mn-Co spinel protective coating on ferritic stainless steels for SOFC interconnect applications

Microstructure and diffusion behavior of Co-Ni-W conversion coating for metallic interconnect of solid oxide fuel cell

Efficient FeCoNi/CeO 2 coatings for solid oxide fuel cell steel interconnect applications

Applying the Protective Mn–Co–La2O3 Coating on Crofer 22 APU Ferritic Stainless Steel Used as Solid Oxide Fuel Cell Interconnects

Fe doped Ni–Co alloy by electroplating as protective coating for solid oxide fuel cell interconnect application

Initial stage oxidation corrosion of commercial ferritic stainless steels with different Cr contents at 650 °C for solid oxide fuel cells

Metallic Co with Reactive Element Oxide Composite Coatings for Solid Oxide Fuel Cell Interconnect Applications

Effect of Cu on the diffusion behavior and electrical properties of Ni-Co conversion coating for metallic interconnects in solid oxide fuel cells

High temperature oxidation and chromium volatilisation of AISI 430 stainless steel coated by Mn-Co and Mn-Co-Cu oxides for SOFC interconnect application

Protective coatings for Cr2O3-forming interconnects of solid oxide fuel cells