Abstract:This article presents a thorough investigation into the synthesis of trimethylolpropane triacrylate (TMPTA) via the esterification reaction of trimethylolpropane (TMP) with acrylic acid using AmberliteTM 120 IR (H+), Amberlyst® 15, and DowexTM 50WX8 resins as heterogeneous catalysts. Preliminary comparative tests explored the impact of air flow on water removal during the reaction and different acid-to-alcohol molar ratios (3:1, 6:1, or 9:1 mol:mol). The findings revealed that introducing air significantly enhances TMPTA yield and -OH group conversion, particularly at a 6:1 acid-to-alcohol molar ratio. Based on cost considerations, AmberliteTM 120 IR (H+) was selected as the preferred catalyst for further optimization. This included evaluating the effect of catalyst loading (10%, 5.0%, and 2.5% w/wtot) and assessing the impact of a pre-drying process on resin efficiency. The study concluded that optimal conditions did not necessitate drying, requiring 120 °C, a catalyst loading of 10% w/wtot, a 4 h reaction time, an acid:alcohol ratio of 6:1 mol:mol, the presence of MEHQ (0.1% mol/molAA), and air bubbling at 6 ± 1 Nl/h. Catalyst recycling was effectively implemented with a slight reduction in catalytic activity over consecutive runs. Furthermore, the study explored a scaled-up system with a mechanical stirrer, demonstrating the potential for multi-hundred grams scale-up. Considerations for optimizing the air flow stripping system are also highlighted. In summary, this study provides valuable insights into designing and optimizing the esterification process for TMPTA synthesis, laying the foundation for potential industrial applications.

Research on the Synthesis of Ditrimethylolpropane Tetraacrylate (Di-Tmpta)

Synthesis of Trimethylolpropane Triacrylat

Catalytic Synthesis of the Ditrimethylolpropane Tetraacrylate by Cation Exchange Resin

Synthesis and Characterization of Trimethylolpropyl Triacrylate

Study on the Preparation Methods of Trimethylolpropane Triacrylate(TMPTA)

Synthesis and Photopolymerization Kinetics of a Novel Monomer: 1,4-Butanediol Bis(alpha-Trimethylsiloxyacrylate): Steric Effect of the alpha-Trimethylsiloxy Substituent on the Reaction Kinetics

Synthesis of the di-trimethylolpropane octanoate

Effects of Active Diluents on Solidifying Process of UV-curing Reaction for Polyurethane Acrylate

Synthesis of Ditrimethylolpropane Acrylate with Low Functionality for Uv-Curable Coatings

Research of Synthesis Process of TDI-TMP Curing Agent by FT-IR

Heterogeneous Brønsted Catalysis in the Solvent-Free and Multigram-Scale Synthesis of Polyalcohol Acrylates: The Case Study of Trimethylolpropane Triacrylate

Synthesis of butanediol dimethylacrylate catalyzed by solid superacid SO2-4/TiO2/La3+

Synthesis and Properties of Crosslinked Polyacrylate Emulsions Modified with TMPTMA

Radical polymerization of methyl methacrylate with 2,2,3-triphenylpropanoic acid as an initiator

STUDIES ON PHOTOGRAFTING OF TRIMETHYLOL PROPANE TRIACRYLATE ONTO THE SURFACE OF LDPE FILMS

Surface Photografting Polymerization Of Trimethylolpropane Triacrylate Onto Ldpe Substrate In Tetrahydrofuran/Water Mixtures

Synthesis and Liquid Crystalline Phase Behavior Investigation of Triphenylene Acrylate Intermediates

Structure Characterization and Reaction Kinetics of TDI-TMP Prepolymer

Preparation and Characterization of Organic Nano-Titanium Dioxide/Acrylate Composite Emulsions by In-Situ Emulsion Polymerization

Allylthioketone Mediated Free Radical Polymerization of Methacrylates

Synthesis and Characterization of a New Polytriazole Resin Derived from N , N -Dipropargyl- p -propargyloxyaniline