Abstract:The oxidation behavior of titanium-tantalumalloys was investigated with respective concentrationsof each element ranging from 0 to 100 wt.%. Alloys wereexposed to argon-20% oxygen at 800 to 1400°C. Theslowest oxidation rates were observed in alloys with5-20% Ta. The oxidation kinetics of alloys containingless than approximately 40% Ta were approximatelyparabolic. Pure Ta exhibited nearly linear kinetics. Alloys containing 50% or more Taexhibited paralinear kinetics. The activation energiesfor oxidation ranged between 232 kJ/mole for pure Ti and119 kJ/mole for pure Ta, with the activation energies of the alloys falling between these values andgenerally decreasing with increasing Ta content. Theactivation energies for oxidation of the end members, Tiand Ta, agree well with published values for the activation energies for diffusion of oxygenin α-Ti and Ta. Scale formation in the alloys wasfound to be complex exhibiting various layers of Ti-,Ta-, and TiTa-oxides. The outermost layer of the oxidized alloys was predominately rutile(TiO2). Beneath the TiO2 grew avariety of other oxides with the Ta content generallyincreasing with proximity to the metal-oxide interface.It was found that the most oxidation-resistant alloys hadcompositions falling between Ti5Ta andTi-15Ta. Although Ta stabilizes the β-phase of Ti,the kinetics of oxidation appeared to be rate limited byoxygen transport through the oxygen-stabilized α-phase.However, the kinetics are complicated by the formationof a complex oxide, which cracks periodically. Tantalumappears to increase the compositional range ofoxygen-stabilized α-phase and reduces both the solubilityof oxygen and diffusivity of Ti in the α- andβ-phases.

Oxidation Kinetics of Magnesium Alloys Treated by Tantalum Ions Implantation

Thermal Oxidation Behaviour of Ti6Al7Nb and Ti6Al4V Alloys

Micro-arc Oxidation Behaviors of AZ91D Magnesium Alloy in Different Electrolytes

Surface Characterization of Thermally Oxidized Titanium Alloys

Influence of Implanted Aluminum Ions on the Oxidation Behavior of M5 Alloy at 500°C

Raising the Oxidation Resistance of Low-Alloyed Mg-Ca Alloys Through a Preheating Treatment in an Argon Atmosphere

In vitro biocompatibility and degradation assessment of tantalum oxide coated Mg alloy as biodegradable implants

Corrosion Resistance and In Vitro Biological Properties of TiO2 on MAO-Coated AZ31 Magnesium Alloy via ALD

Retardation of Surface Corrosion of Biodegradable Magnesium-Based Materials by Aluminum Ion Implantation

Composition Dependence of the Kinetics and Mechanisms of Thermal Oxidation of Titanium-Tantalum Alloys

Surface Characterization of New β Ti-25Ta-Zr-Nb Alloys Modified by Micro-Arc Oxidation

Improvement in Corrosion Resistance of Tantalum Oxide and Tantalum Oxide with Diethanolamine Sol–Gel Coated Magnesium Alloys

Study on Micro-arc Oxidation of Mg-Zn-Y-Nd-Ca Magnesium Alloys

Coating Formation on Ti-6Al-4V Alloy by Micro Arc Oxidation in Molten Salt

The Effect of Thermal Oxidation on the Photothermal Conversion Property of Tantalum Coatings

Mechanism of microarc oxidation on AZ91D Mg alloy induced by β-Mg17Al12 phase

Effects of Sodium Tungstate on Properties of Micro-Arc Coatings on Magnesium Alloys

Corrosion resistance enhanced by an atomic layer deposited Al2O3 /micro-arc oxidation coating on magnesium alloy AZ31

Properties of Titanium Oxide Coating on MgZn Alloy by Magnetron Sputtering for Stent Application

Growth Process and Dielectric Breakdown of Micro Arc Oxidation Coating on AZ31 Mg Alloy Pretreated by Alkali Treatment

XPS Investigation of the Oxidation States of the As-Deposited Ta Films Prepared by Magnetron Sputtering Technology