Abstract:We report on the observation of a very low growth velocity of single-walled carbon nanotubes (SWNTs) and consequently the direct length-sorted growth and patterned growth of SWNTs by using a metal-catalyst-free chemical vapor deposition (CVD) process proposed recently by our group, in which SiO(2) serves as catalyst. We found that the growth velocity of the SWNTs from SiO(2) catalyst is only 8.3 nm/s, which is about 300 times slower than that of the commonly used iron group catalysts (Co as a counterpart catalyst in this study). Such a slow growth velocity renders direct length-sorted growth of SWNTs, especially for short SWNTs with hundreds of nanometers in length. By simply adjusting the growth duration, SWNTs with average lengths of 149, 342, and 483 nm were selectively obtained and SWNTs as short as approximately 20 nm in length can be grown directly. Moreover, comparative studies indicate that the SiO(2) catalyst possesses a much longer catalytic active time, showing sharp contrast with the commonly used Co catalyst which quickly loses its catalytic activity. Taking advantage of the very slow growth velocity of the SiO(2) catalyst, patterned growth of SWNT networks confined in a narrow region of <5 microm was also achieved. The short SWNTs may show intriguing physics owing to their finite length effect and are attractive for various practical applications.

Growth velocity and direct length-sorted growth of short single-walled carbon nanotubes by a metal-catalyst-free chemical vapor deposition process.

Ultrafast growth of single-crystalline Si nanowires

Metal-catalyst-free growth of single-walled carbon nanotubes.

Direct Growth of Single-Walled Carbon Nanotubes without Metallic Residues by Using Lead as a Catalyst

CVD catalytic growth of single-walled carbon nanotubes with a selective diameter distribution

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

High-Density Growth of Single-Wall Carbon Nanotubes on Silicon by Fabrication of Nanosized Catalyst Thin Films

How Catalysts Affect the Growth of Single-Walled Carbon Nanotubes on Substrates

Thin-Film Metal Catalyst For The Production Of Multi-Wall And Single-Wall Carbon Nanotubes

Possible Tactics to Improve the Growth of Single-Walled Carbon Nanotubes by Chemical Vapor Deposition

Growth of Single-Walled Carbon Nanotubes from Discrete Catalytic Nanoparticles of Various Sizes

Growth Of High-Quality Single-Wall Carbon Nanotubes Without Amorphous Carbon Formation

Diameter controlled growth of single-walled carbon nanotubes from SiO2 nanoparticles

Study of Controlled Growth of Carbon Nanotubes in Microstructures at Low Temperature

Influence of Cerium Metal As Catalyst on the Growth and Structure of Single-Walled Carbon Nanotubes

Low-Temperature, Directly Depositing Individual Single-Walled Carbon Nanotubes for Fabrication of Suspended Nanotube Devices

Growth modes of single-walled carbon nanotubes on catalysts

Fabrication of Ultralong and Electrically Uniform Single-Walled Carbon Nanotubes on Clean Substrates

CVD Growth of Carbon Nanotube Forest with Selective Wall-Number from Fe–Cu Catalyst

Narrow-chirality distributed single-walled carbon nanotube synthesized from oxide promoted Fe–SiC catalyst

Discrete Growth of Single-walled Carbon Nanotubes on Surfaces