Study on equal channel angular pressing process of Mg–Zn–Y–Mn–Ti magnesium alloy enhanced by lamellar LPSO phase and spherical W phase
Jianqiang Hao,Li zhao,Jinshan Zhang,Hongxia Wang,Weili Cheng,Boqiong Li,Yang Bai
DOI: https://doi.org/10.1016/j.jmrt.2023.07.089
IF: 6.267
2023-07-27
Journal of Materials Research and Technology
Abstract:To solve the problem of internal surface cracking problem during equal channel angular pressing (ECAP), this study modified a conventional die. The dies before and after modification were compared and analyzed by using DEFORM-3D software. Finally, a modified ECAP die was manufactured to investigate the effect of different number of pressed passes on the microstructure and mechanical properties of the solution-treated Mg 93.5 Zn 2.5 Y 2.5 Mn 1 Ti 0.5 alloy. The results show that the volume fraction of dynamically-recrystallized grains continuously increases while the volume fraction of W phase continuously decreases with the increase of pressed passes. The size of recrystallized grains initially decreases and then increases, reaching the minimum after 6 pressing passes. The basal texture of (0002) initially decreases, then increases and finally decreases, and the basal texture of 6-pass pressed sample displays the strongest texture. The yield strength and tensile strength of the alloy increase initially and then decrease, while the elongation increases continuously. After 6 pressing passes, the alloy exhibits excellent comprehensive mechanical properties, with a yield strength of 251 MPa, a tensile strength of 340 MPa and an elongation of 26.1%.
materials science, multidisciplinary,metallurgy & metallurgical engineering