Abstract:Traditional poly(ether sulfone) (PES) membranes and spheres exhibit asymmetrical and non-interconnected porous structures, which results in relatively low mass transfer efficiency and thus limits their applications in separation and adsorption to some extent. In this work, PES-based monolithic materials are fabricated by a simple method termed freezing-induced phase separation (FIPS). The as-prepared monoliths show a uniform and interconnected porous structure, high porosity (73.11-83.32%), and good mechanical properties (Young's modulus higher than 3.70 MPa). A hydrophilic copolymer (poly(2-aminoethyl methacrylate)& horbar;PAMA) of acrylic acid (AA) and methyl methacrylate (MMA) is introduced into the monolith, which improved the hydrophilicity and endowed the modified PES-based monolith with a negatively charged surface. The pseudo-ternary PES/PAMA, EtOH, and N,N-dimethylformamide (DMF) systems are studied. The monoliths show a denser and more uniform porous structure when a relatively high PES concentration and PAMA amount are used. The adsorption capacity of monoliths for methylene blue (MB) increases with increasing PAMA content, from 10.26 to 64.38 mg/g. Meanwhile, the adsorption capacity can be further improved by hot water post-treatment, from 64.38 to 108.33 mg/g. Batch adsorption tests indicate that the adsorption behavior of the MB monoliths fit the pseudo-second-order kinetic and Langmuir isotherm models. The dynamic adsorption results indicate that the monoliths could remove MB rapidly and effectively. In addition, the modified PES-based monolith selectively adsorb the cationic dyes in a mixed dye solution and has good recyclability.

Polyethersulfone-Modified Montmorillonite Hybrid Beads for the Removal of Bisphenol A

Preparation of Polyethersulfone–organophilic Montmorillonite Hybrid Particles for the Removal of Bisphenol A

Matrix-enhanced Adsorption Removal of Trace BPA by Controlling the Interlayer Hydrophobic Environment of Montmorillonite

Adsorption Properties of Polyethersulfone-Modified Attapulgite Hybrid Microspheres for Bisphenol A and Sulfamethoxazole

Enhanced removal of bisphenol A from aqueous solution by aluminum-based MOF/sodium alginate-chitosan composite beads

PERFORMANCE OF Bi2WO6@MXenes-NS ACTIVATED PERMONOSULFATE IN DEGRADING BISPHENOL A

Effective adsorption of bisphenol A from aqueous solution over a novel mesoporous carbonized material based on spent bleaching earth

Preparation of Polyethersulfone-Modified Sepiolite Hybrid Particles for the Removal of Environmental Toxins

Preparation Of Polyethersulfone/Sulfonated Polyethersulfonephenylethane Microspheres And Its Application For The Adsorption Of Bisphenol A

Enlargement of Uniform Micropores in Hierarchically Ordered Micro–mesoporous Carbon for High Level Decontamination of Bisphenol A

Polysulfone-Activated Carbon Hybrid Particles For The Removal Of Bpa

Removal of bisphenol A by adsorption mechanism using PES-SiO2 composite membranes

Adsorption properties of polyethersulphone/modified attapulgite hybrid microspheres for bisphenol A

Simultaneous Adsorption Of Cd2+ And Bpa On Amphoteric Surfactant Activated Montmorillonite

Modification and Application of Mesoporous Carbon Adsorbent for Removal of Endocrine Disruptor Bisphenol A in Aqueous Solutions

Organo-montmorillonites for efficient and rapid water remediation: sequential and simultaneous adsorption of lead and bisphenol A

Adsorption Characteristics of Bisphenol A from Aqueous Solution Onto HDTMAB-Modified Palygorskite

Study on the Adsorption of Environmental Toxins Ethidium Bromide and Bisphenol A by Polyethersulfone/Modified Sepiolite Hybrid Particles

The Selective Removal of Bisphenol A Using a Magnetic Adsorbent Fused with Bisphenol A-Binding Peptides

Poly(acrylic Acid-Co-methyl Methacrylate)-Modified Poly(ether Sulfone) Porous Monolith Fabricated Using a Freezing-Induced Phase Separation Method

Bisphenol A and 17α-Ethinylestradiol Removal from Water by Hydrophobic Modified Acicular Mullite