Preparation and application processes of difunctional hollow fiber composite membranes with catalysis and pervaporation

XU Zhenliang,MA Xiaohua,WEI Yongming,CHENG Liang

DOI: https://doi.org/10.3969/j.issn.1007-8924.2011.03.033

2011-01-01

Abstract:Difunctional hollow fiber composite membranes(PFSA-PVA-SiO2(Al2O3 and TiO2)/PVA/PAN) with catalysis and pervaporation(PV) were prepared,in which employed PAN as support membrane,PVA as separative layer,and PFSA-PVA-nanoparticles(SiO2,Al2O3 and TiO2) as catalytic layer.The separation performances of difunctional membranes were investigated by dehydrating the top product of ethanol-acetic acid esterifiaction reaction,the catalytic activities of them were studied through ethanol-acetic acid esterification reaction,and the distillation performances of single functional pervaporation membranes as structural packings were explored by separation ethanol-water solution.The results showed that both of the separative and catalytic layers were coated on the PAN support membrane tightly;the difunctional membranes had remarkably separation performances in terms of permeation fluxes [approximately 170 g/(m2· h)] and separation factors(separation factors of water to ethanol were all higher than 27,and no ethyl acetate permeated);the difunctional membranes had good catalytic activities and the ethanol-acetic acid esterification conversion could reach to 56.5% when using them as catalyst.When used single functional pervaporation membranes as structural packings in distillation,the HTU was decreased significantly(lower than 10 cm) compared with conventional distillation packings,and the gas and liquid on either side of the hollow fiber(tube side or shell side,in literatures) or both on the shell side(in this experiment) had little influences on HTU.