Abstract:The widespread use of sodium aluminosilicate glass in many engineering applications due to its mechanical and optical properties (transparency, dielectric, etc.), has become common in recent years. However, glass, a brittle material, has its vulnerability to fracture. Processes such as heat treatment (heat tempering) or chemical strengthening through ion-exchange have been used to create residual stress profiles on the glass, in a bid to improve its fracture strength. However, failure still occurs, which is mostly catastrophic and expensive to repair. Therefore understanding, predicting, and eventually improving the resistance to damage or fracture of chemically strengthened glass is important to designing new glasses that would be tougher while retaining their transparency. The relationship between the glass residual stress parameters such as the compressive stress (CS), depth of compression layer (DOL), and central tension (CT) versus apparent (effective) fracture toughness for different crack depth was investigated in this study using a Silicon Carbide particle blast plus ring-on-ring (RoR) test method. The results also showed that improving the fracture resistance of glass via chemical strengthening requires a proper combination of CS, DOL, and CT, which is particularly dependent on the initial/existing crack (flaw) depth. It was determined that for a damage event involving the introduction of a shallow crack depth, the criterion for optimal resistance to fracture, in terms of apparent fracture toughness, is weighted more towards a high CS, than deep DOL while for a deep flaw damage event, it is more weighted towards deep DOL, than a high CS. These results provide a valuable piece of information in the design of a more robust glass in engineering applications.

Influence of the Load Conditions on the Failure Wave in Glasses

Microstructure damage of glasses under shock wave compression

Soft Impact Response of Laminated Glass Plates

Bridging necking and shear-banding mediated tensile failure in glasses

Fatigue endurance limit and crack front evolution in metallic glass

Fracture of brittle solids under impact: The decisive role of stress waves

Intermittent in-situ high-resolution X-ray microscopy of 400-nm porous glass under uniaxial compression: study of pore changes and crack formation

A Stochastic Analysis of Glass Crack Initiation under Thermal Loading

Shock induced damage and damage threshold of optical K9 glass investigated by laser-driven shock wave

The Competing Effect of Initial Crack Depth Versus Chemical Strengthening Parameters on Apparent Fracture Toughness of Sodium Aluminosilicate Glass

A study on the damage characteristics of glass under the combined effects of explosion and high temperature: An analysis using peridynamics

De Lamination And Fatigue Crack Growth Behavior In Fiber Metal Laminates (Glare) Under Single Overloads

Ductile Fracture of Bulk Metallic Glass Zr 50 Cu 40 Al 10 under High Strain-Rate Loading

The Dynamic Response of Brittle Materials under Impact Loading

Influences of temperature and impacting velocity on dynamic failure of laminated glass: Insights from peridynamic simulations

Crack-tip strain field mapping and the toughness of metallic glasses

Spallation fracture dependence on shock intensity and loading duration in single-crystal aluminum

Fatigue failure in glasses under cyclic shear deformation

The Failure Stress of Bulk Metallic Glasses under Very High Strain Rate

The effect of initial densification on the spallation damage of silica glass induced by planar impact

Characterizing damage patterns and evolution in Multi-Hole GLARE laminates under tensile load via integrated AE and DIC techniques