Abstract:A convenient method was developed to fabricate gold nanoparticles loaded microcapsules in one step and with high efficiency. First of all, the old colloidal solution was prepared through reduction of AuCl- ions with NaBH4 under stirring, and poly( vinylpyrrolidone) ( PVP) was added quickly under severe agitation to prevent the aggregation of the gold nanoparticles during the dialyses. The gold nanoparticles lit the colloidal solution had a diameter of about 7 mm and had a maximum absorption at 5 16 run. Next, template polymerization of acrylic acid (AA) lit the presence of PVP and 3-(trimethoxysilyl) propyl methacrylate (MPS) modified silica particles was carried out in the gold colloidal solution. The polymerization was initiated by K2S2O8 and maintained for about 2 h Under nitrogen atmosphere. After polymerization, the resulting composite particles were separated from the dispersion through centrifugation and were washed with triply-distilled water for several times. Finally, the gold nanoparticle-loaded microcapsules were obtained after core-removal with HF. In this process the pre-adsorption of the complex of PVP/AA onto the gold nanoparticles made the nanoparticles polymerizable with free AA monomers during the template polymerization,and the gold nanoparticles doped PAA/PVP complex films were formed on the surfaces of the silica particles. After the core-removal process, the hollow nature and the integrity of the obtained microcapsules in both dry and wet states were demonstrated by scanning electron microscopy and confocal laser scanning microscopy, respectively. The entrapment of the gold nanoparticles in the capsules was con-firmed by transmission electron microscopy. Electron diffraction pattern of the nanoparticles-loaded microcapsules showed the gold polycrystalline diffraction rings, from which the lattice constant of crystal plane vertical bar 1 1 1 vertical bar was calculated as 0.4174 nm, further confirming the existence of the gold nanoparticles. The gold nanoparticles were distributed uniformly in the microcapsule shells with 110 Sign of aggregations. The amount of nanoparticles loaded in the microcapsule shells could be tuned by the concentration of the gold colloidal solution, i. e. higher concentration resulted ill microcapsules with larger amount of gold nanoparticles in the shells. This process can be extended to other types of nanoparticles and polymers, thus can be widely applied to obtain composite microcapsules with desired functions.

One-pot Synthesis of Polyacrylamide-Gold Nanocomposite

Preparation of Reversibly Photo-Cross-Linked Nanogels from Ph-Responsive Block Copolymers and Use As Nanoreactors for the Synthesis of Gold Nanoparticles

One-step synthesis and characterization of gold nanoparticles doped polyacrylamide hydrogels

Preparation Of Uniformly Dispersed N-Isopropylacrylamide/Acrylic Acid/Nanosilver Composite Hydrogel And Its Anti-Mold Properties

Preparation and structure of poly(styrene-acrylonitrile)/montmorillonite nanocomposite

Facile One-Pot Synthesis of Gold Nanoparticles Stabilized with Bifunctional Amino/siloxy Ligands

Preparation and study of polyacryamide-stabilized silver nanoparticles through a one-pot process.

A novel synthetic route to metal–polymer nanocomposites by in situ suspension and bulk polymerizations

Effect of Thermo‐ and pH‐sensitive Block Copolymer Structure and Composition on the Synthesis and Stabilization of Gold Nanoparticles

Preparation of Polymer–nanoparticle Composite Beads by a Nanoparticle-Stabilised Suspension Polymerisation

Fabrication and Characterization of Au-Polyacr ylamide Nanocomposites by a Convenient Ultraviolet Irradiation Technique

Preparation of Hybrid Polymer Nanocomposite Microparticles by a Nanoparticle Stabilised Dispersion Polymerisation

Amphiphilic multiblock copolymer stabilized Au nanoparticles

One-Step Preparation of Fibrous Aggregates of Gold Nanoparticles Using Aniline As Reducing Agent As Well As Monomer

A One-Pot Method to Prepare Gold Nanoparticle Chains with Chitosan

Synthesis and Structural Control of Gold Nanoparticles-Coated Polystyrene Composite Particles Based on Colloid Thermodynamics

Aqueous (co)polymer stabilisers for size-controlled 2-5 nm gold nanoparticle synthesis with tuneable catalytic activity

FABRICATION AND CHARACTERIZATION OF GOLD NANOPARTICLES LOADED MICROCAPSULES

Facile and controlled fabrication of functional gold nanoparticle-coated polystyrene composite particle

Block-Random Copolymer-Micellization-Mediated Formation of Polymeric Patches on Gold Nanoparticles

Novel Electrochemical Method for Synthesis of Nanostructured Materials of Noble Metals Based on Poly(N-Vinylpyrrolidone) (PVP)