Abstract:Polymer-coated gold nanoparticles (PNIPAM-AuNPs) with temperature sensitive and intelligent fluorescent properties were prepared by ligand exchange between dimethylaminochalcone-terminated poly(N-isopropylacrylamide) (PNIPAM-DMAC) and 4-dimethylaminopyridine-stabilized gold nanoparticles (DMAP-AuNPs) precursor, and the morphology and structure of the as-prepared AuNPs were analyzed by UV-Vis, TEM, H-NMR, FTIR and TGA. The as-synthesized PNIPAM-AuNPs can be well dispersed not only in water but also in ethanol, acetone, chloroform and tetrahydrofuran, and the corresponding characteristic peak of the surface plasmon resonance (SPR) absorption of the PNIPAM-AuNPs is observed at 537 nm,527. 6 nm, 527. 4 nm, 532. 2 nm and 530. 4 nm respectively. The surface grafting density of PNIPAM-DMAC is 1-2 polymer chains/nm(2). The results of thermosensitive properties show that PNIPAM-AuNPs have a lower critical solution temperature (LCST) 2. 5 K lower than that of PNIPAM-DMAC, and the SPR absorption peak of PNIPAM-AuNPs blueshifts to 525 nm from 537 nm after the phase transition. With the increase of the solvent polarity, the fluorescence characteristic wavelength of PNIPAM-AuNPs redshifts, and the fluorescence intensity first increases then decreases, which indicates solvent polarity sensitive fluorescence properties of PNIPAM-AuNPs. There are no fluorescent emitting properties of PNIPAM-AuNPs aqueous solution at 25 CC, while at 45 CC the fluorescence intensity of PNIPAM-AuNPs enhances obviously,which endows PNIPAM-AuNPs with temperature "on/off" fluorescent properties.

Fabrication and Characterization of Au-Polyacr ylamide Nanocomposites by a Convenient Ultraviolet Irradiation Technique

A Convenient Ultraviolet Irradiation Technique For Fabrication Of Silver-Polymer Nanocomposites

Inorganic-organic polymer nanocomposites fabricated by ultraviolet irradiation

Preparation Of Uniformly Dispersed N-Isopropylacrylamide/Acrylic Acid/Nanosilver Composite Hydrogel And Its Anti-Mold Properties

A Novel in Situ Ultraviolet Irradiation Polymerization–Photolysis Technique for Fabrication of Polyacrylamide-MS (M = Cd, Pb, Zn) Nanocomposites at Room Temperature

In Situ Controlled Synthesis of Thermosensitive Poly(N-Isopropylacrylamide)/Au Nanocomposite Hydrogels by Gamma Radiation for Catalytic Application

In situ single-step synthesis of gold/polyacrylamide nanocomposites in an ethanol system

One-step synthesis and characterization of gold nanoparticles doped polyacrylamide hydrogels

Preparation and characterization of polyacrylamide–silver nanocomposites

Preparation of polyacrylamide and gamma-zirconium phosphate nanocomposites by intercalative polymerization.

Γ-Radiation Synthesis and Characterization of Polyacrylamide–silver Nanocomposites

Preparation of Silver Nanocomposites Stabilized by an Amphiphilic Block Copolymer under Ultrasonic Irradiation

Polyacrylamide–metal nanocomposites: one-pot synthesis, antibacterial properties, and thermal stability

Preparation of Gold Nanoparticles in N, N-dimethylformamide in the Presence of Methyl Ester Terminated Poly(amidoamine) Dendrimers

Studies on the preparation and structure of polyacrylamide/α-zirconium phosphate nanocomposites

Synthesis and characterization of polyacrylamide–nickel amorphous nanocomposites by γ-irradiation

Amphiphilic multiblock copolymer stabilized Au nanoparticles

Nonaqueous solution route to synthesis of polyacrylamide-silver nanocomposites at room temperature

In Situ Preparation of Au or Ag Nanoparticles in the Presence of Hyperbranched Poly(amidoamine)s with Hydrophobic End‐groups As Nanoreactors and Reductants

Studies on Polymer-coated Gold Nanoparticles with Temperature Sensitive and Intelligent Fluorescent Properties

A novel preparation method of polyaluminum chloride/polyacrylamide composite coagulant: Composition and characteristic