Synthesis and assembly of gold nanoparticle-doped polymer solid foam films at the liquid/liquid interface and their catalytic properties.

Lan-Jun Chen,Huihui Ma,Kuangcai Chen,Hyeong-Rae Cha,Yong-Ill Lee,Dong-Jin Qian,Jingcheng Hao,Hong-Guo Liu
DOI: https://doi.org/10.1016/j.jcis.2011.06.037
IF: 9.9
2011-01-01
Journal of Colloid and Interface Science
Abstract:Gold nanoparticle-doped poly(2-vinylpyridine) (P2VP) microcapsules and foam films were synthesized and assembled at the P2VP chloroform solution/HAuCl(4) aqueous solution interface at 25 °C. It was found that Au nanoparticles with the average diameter of 2.1 nm were homogeneously embedded in and adsorbed on the walls of the capsules and foams, the nanoparticles were composed of Au(0) and Au(III) with the molar ratio of about 75/25, and the mass percent of Au elements was measured to be 19.65%. The formation of the nanostructures was attributed to the self-assembly of P2VP at the liquid/liquid interface, the simultaneous reduction of AuCl(4)(-) ions by a small amount of ethanol in the chloroform and adsorption of AuCl(4)(-) ions. After irradiated by UV-light for 1h, the average diameter of the nanoparticles was found to be 2.2 nm, and the AuCl(4)(-) ions were transformed to Au(0) completely. The catalytic performance of these composite nanostructures were evaluated by using the reduction of 4-nitrophenol (4-NP) by potassium borohydride in aqueous solutions. The catalytic activity was very high in the first cycle, decreased rapidly and slightly in the second and third cycles, respectively, due to the aggregation of some nanoparticles, and stabilized after the third cycle.
What problem does this paper attempt to address?