Abstract:A facile and "green" method was proposed to introduce Ag nanoparticles (Ag NPs) into the hierarchically monolithic silica uniformly in the presence of (3-aminopropyl)-triethoxysilane (APTES) and ethylene glycol. APTES is used to modify the monolith by incorporating amino groups onto the surface of meso-macroporous skeletons, while ethylene glycol is employed as the productive reductant. Ag NPs are homogeneously immobilized in hierarchically monolithic silica after reduction and drying at 40 degrees C for different duration times, and the embedded amount of Ag NPs can reach 15.44 wt% when treated once. The embedment of Ag NPs increases with the repeat treatment and the APTES amount, without uncontrollable crystalline growth. The surface areas of Ag NPs embedded in silica monoliths after heat treatment at 300 and 400 degrees C are higher than those before heat treatment. The modification via APTES and the embedment of Ag NPs does not spoil the morphology of monolithic silica, while changing the pore structures of the monolith. A tentative formation process and a reduction mechanism are proposed for the modification, reduction and embedment. Ag NPs embedded in monolithic silica is promising for wide applications such as catalysis and separation.

One-Step Preparation of Fibrous Aggregates of Gold Nanoparticles Using Aniline As Reducing Agent As Well As Monomer

One-step Controlled Synthesis of Anisotropic Gold Nanostructures with Aniline As the Reductant in Aqueous Solution.

Facile Synthesis of Gold Nanoplates by Thermally Reducing AuCl4- with Aniline

Facile One-Pot Synthesis of Gold Nanoparticles Stabilized with Bifunctional Amino/siloxy Ligands

Preparation and Microstructure of Silver Nanopowder with Spheric Morphology

A Controlling Method For Agi Nanoparticles Preparation Using Combinatorial Surfactants

Facile Preparation of Silver Nanoparticles Homogeneously Immobilized in Hierarchically Monolithic Silica Using Ethylene Glycol As Reductant

Layered Assemblies of Single Crystal Gold Nanoplates: Direct Room Temperature Synthesis and Mechanistic Study

One-Step Synthesis and Characterization of Polyelectrolyte-Protected Gold Nanoparticles Through A Thermal Process

In Situ Preparation of Au or Ag Nanoparticles in the Presence of Hyperbranched Poly(amidoamine)s with Hydrophobic End‐groups As Nanoreactors and Reductants

Layered Aggregates of Gold Nanoparticles: Solution and Surface-Assembled Structures

Polyphenol-grafted collagen fiber as reductant and stabilizer for one-step synthesis of size-controlled gold nanoparticles and their catalytic application to 4-nitrophenol reduction

Facile Controlled Preparation of Gold Nanoparticles with Amphiphilic Thiacalix[4]arene As Reductant and Stabilizer.

Facile synthesis of micrometer-sized gold nanoplates through an aniline-assisted route in ethylene glycol solution

Ammonium Bicarbonate Reduction Route to Uniform Gold Nanoparticles and Their Applications in Catalysis and Surface-Enhanced Raman Scattering

A One-Pot Method to Prepare Gold Nanoparticle Chains with Chitosan

One-Step Synthesis and Size Control of Dendrimer-Protected Gold Nanoparticles: A Heat-Treatment-Based Strategy

Synthesis of Gold Nanomaterials with Different Morphologies

Linear Aggregation of Gold Nanoparticles in Ethanol

Facile synthesis of gold nanoflowers with high surface-enhanced Raman scattering activity

One‐step Synthesis of Ag@PS Nanospheres Via Flash Nanoprecipitation