Abstract:Layered aggregates of gold nanoparticles were synthesized by injection of a methanol solution of HAuCl4 into a mixture of octadecene (ODE) and oleylamine (OLA) at high temperature under the flow of argon, followed by sedimentation out of a toluene/ethanol mixture solvent. Interconnection of the nanoparticles into single-layered and multilayered aggregate structures was revealed by transmission electron microscopy (TEM). Two ultraviolet-visible-near-infrared (UV-vis-NIR) extinction peaks, centered at 541 and 685 nm, were observed for a toluene dispersion of the aggregates, which could be assigned as transverse and extended surface plasmon resonance bands. To expand the utility of the aggregates, a surface assembly of the structure onto amine modified oxide surfaces was carried out. UV-vis-NIR extinction spectroscopy, scanning electron microscopy (SEM), and atomic force microscopy (AFM) were employed to characterize the surface-anchored structures and confirm the layered nature of the aggregates. Such surface structures could be utilized as effective surface-enhanced Raman scattering (SERS) substrates, pointing to a potentially new enabling technology for the preparation of optically active media.

Layered Aggregates of Gold Nanoparticles: Solution and Surface-Assembled Structures