Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Shape-tailored Photoluminescent Intensity of Red Phosphor Y2O3:Eu3+

Synthesis of Nanometer Y2o3 : Eu Phosphor and Its Luminescence Property

Synthesis and luminescence properties of Y 2O 3:Eu with flower-like microstructure

Two-steps Prepared Monodisperse Li-doped Y2O3:Eu3+ Microspheres and Their Luminescence Properties

Luminescent Properties of Y2O3:Eu Synthesized by Sol–gel Processing

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

Preparation and Properties of Ti, Eu Co-Doped Y2O2S:0.06Ti,0.08Eu Phosphor with Red Long Afterglow

Novel Red-Emitting Eu3+-Doped Y2(WxMo1-xO4)3 Phosphor with High Conversion Efficiency for Lighting and Display Applications

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

Synthesis and Luminescence Properties of New Red-Emitting Phosphors YGe0.5M0.5O4:Eu3+ (m=mo, W)

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Local Structure and Luminescence of Nanocrystalline Y2O3:Eu

New Red Phosphor with A High Color Purity: Controlled Synthesis of 3d Architectures of Yw2o6(Oh)(3) : Eu

Formation mechanism and red light emission photoluminescence of single-phase crystalline Eu2O2CO3 nanoplates compared with Y2O3:Eu phosphor

Hydrothermal synthesis and tunable luminescence of YPO4:Eu2+/Eu3+, Tb3+ nanocrystals

Red Photoluminescence and Morphology of Eu3+ Doped Ca3La3(BO3)5 Phosphors

Synthesis and Properties of Europium-Based Phosphors on the Nanometer Scale: Eu2O3, Gd2O3:Eu, and Y2O3:Eu.

Optical properties, energy transfer and thermal stability of spherical nano-phosphor YPO4:Eu3+:Sm3+

A new strategy to the NaY(MoO4)2:Eu3+ phosphors modified by tetraethyl orthosilicate for LEDs: Photoludminescence properties and morphology

Synthesis of red-luminescent Eu3+-doped lanthanides compounds hollow spheres

SYNTHESIS OF Y_2O_3∶Eu NANOCRYSTALLINE BY COMPLEX PRECURSORS