Abstract:Well-defined porous Co3O4 nanodendrites have been synthesized by a simple one-pot hydrothermal method combined with subsequent calcination. Importantly, after thermal treatment, the dendritic morphology could be completely preserved. The as-obtained superstructures are characterized by several techniques, such as powder X-ray diffraction, Fourier transform infrared spectroscopy, X-ray photoemission spectroscopy, elemental analysis, transmission electron microscopy, high-resolution TEM and magnetometry. On the dendritic hierarchical structures, a number of nanorods with different lengths and widths are connected to the main trunk with a diameter of about 50 nm and length of several micrometers. Each branch is about 0.5-1.0 mm with a width ranging from 100 to 400 nm. The possible formation mechanism was proposed on the basis of the contrasting experiments. It demonstrated that trisodium citrate and acetone play important roles in the synthesis of Co3O4 nanodendrites, while the other reaction parameters, such as reaction temperature, concentration of trisodium citrate and reaction time, have close relationships with the final morphology of the Co3O4 products. Optical properties of Co3O4 nanodendrites were characterized by Raman and UV-vis spectroscopy. Magnetic property measurement shows that Co3O4 nanodendrites have a low Neel transition temperature of 35 K. The as-prepared mesoporous Co3O4 nanostructures are expected to have great applications in many fields.

Preparation of rod-like and polyhedron-like Co_3O_4 powders via hydrothermal treatment followed by decomposition

Preparation of Nanosized GdCoO 3 Powder Using Amorphous Heteronuclear Complex As a Precursor

Preparation and Electrochemical Performance of Nanosized Co3O4 Via Hydrothermal Method

Shape-controlled Synthesis of Nanocubic Co3O4 by Hydrothermal Oxidation Method

Synthesis and Their Physicochemical Behaviors of Flower-Like Co3O4 Microspheres

Synthesis of Co3o4 Nanorod Bunches from A Single Precursor Co(Co3)(0.35)Cl-0.20(Oh)(1.10)

Hydrothermal Preparation of CuAlO2 Powder

Study on thermodynamic equilibrium and character inheritance of cobalt carbonate decomposition

Preparation of nanosized LaCoO3 perovskite oxide using amorphous heteronuclear complex as a precursor at low temperature

Preparation of MoO 3 powder by hydrothermal method

Synthesis of PbZrO3 Powder by a COprecipitation Method

Preparation of Nanocrystalline Co3O4 and Its Catalytic Performance for Thermal Decomposition of Ammonium Perchlorate

Structure and Catalytic Activity of 3D Macro/mesoporous Co3O4 for CO Oxidation Prepared by a Facile Self-Sustained Decomposition of Metal–organic Complexes

High-Yield Preparation of Uniform Cobalt Hydroxide and Oxide Nanoplatelets and Their Characterization

Synthesis And Characterization Of Ca2co2o5 Powders By Coprecipitation Method

Novel three-dimensional Co3O4 dendritic superstructures: Hydrothermal synthesis, formation mechanism and magnetic properties

Cobalt hydroxide nanosheets and their thermal decomposition to cobalt oxide nanorings.

Preparation of Α-Mn2o3 and MnO from Thermal Decomposition of MnCO3 and Control of Morphology

Moderate temperature synthesis of nanocrystalline Co3O4 via gel hydrothermal oxidation

Preparation of nanosized CoAl2O4 powders by sol–gel and sol–gel-hydrothermal methods

Morphology-controlled synthesis of Co3O4 crystals by soft chemical method