Effect of Co on morphology and preparation of in situ synthesis of WC-Co composite powders
ErTao Zhu,JiuXing Zhang,ShengDa Guo,XinYu Yang,Xiang Zhang,JianGao Yang
DOI: https://doi.org/10.1088/2053-1591/ab1c38
IF: 2.025
2019-05-08
Materials Research Express
Abstract:The WC and WC-Co composite powders were fabricated through spray-drying, calcinations as well as byreduction and carbonization treatment using the precursors, AMT, C 6 H 12 O 6 , Co(CH 3 COO) 2 · 4H2 O and H 2 O with different Co content (0, 4, 6, 8, 12 wt%). The results show that the obtained WCby the spray-drying method were nearly spherical with a smooth surface and maintaining the sphericalstructure of AMT. Also, the loose cobalt oxide powders prepared by the calcinations of precursorshad uniform structures with good dispersivity, and higher degree of sphericity when Co content wasgreater than 6 wt%. Moreover, aggregates with original sheet structure exist in the WC and WCcomposite powders prepared by reduction and carbonization, and also higher the Co content, the moreobvious the agglomeration. Using XRD, EDS and XPS, activated carbon, WO 3 and Co 3 O 4 with a smallcontent ...
materials science, multidisciplinary