Abstract:In this study, pure cobalt oxide (Co 3 O 4 ) nanoparticles were synthesized using a simple hydrothermal approach. The effect of the reducing agent and reaction temperatures of the prepared products were examined. Co 3 O 4 is formed in the as-synthesized sample, at reaction temperature 190 °C was observed in the XRD pattern. The XPS survey scan spectrum showed the distinctive peaks of the Co and O elements and their valence states. FESEM and HRTEM revealed the particles as cubical in nature. Peak associated with the elements Co and O on the EDAX spectrum demonstrated the purity of the nanoparticles. Three electrode setups were used to measure the electrochemical properties of the synthesized nanoparticles. DTA curve corresponding exothermic peak at 225 °C and the crystallization of the final product was attributed for the third weight loss of 1.5 % in the temperature range of 280 °C to 450 °C. Formation of Co 3 O 4 was confirmed by the observed XRD diffraction peaks at 2 θ = 36.83°, 59.82°, and 65.30°, which correspond to h k l planes (311), (511) and (440), respectively. The high-resolution Co2p spectra showed two prominent spin-orbital peaks, 2p 1/2 and 2p 3/2 , at 796.37 eV and 781.81 eV, respectively. The increase in temperature causes the particle size to grow ranges between 20 and 70 nm and the average particle size distribution in the TEM image is 42 nm. The integral area of the CV curve was measured during the CV measurement and as the as-prepared Co 3 O 4 electrode displays specific capacitance values of 154, 126, 81, 65, and 49 Fg −1 at various scan rates of 10, 20, 50, 70, and 100 mVs −1 , respectively.

High-Yield Preparation of Uniform Cobalt Hydroxide and Oxide Nanoplatelets and Their Characterization

Preparation And Magnetic Properties Of Cowo4 Nanocrystals

Cobalt hydroxide nanosheets and their thermal decomposition to cobalt oxide nanorings.

General Solution Route for Nanoplates of Hexagonal Oxide or Hydroxide

Fabrication of morphology and crystal structure controlled nanorod and nanosheet cobalt hydroxide based on the difference of oxygen-solubility between water and methanol, and conversion into Co3O4

Hydrothermal Synthesis of Cobalt Particles with Hierarchy Structure and Physicochemical Properties

Hydrothermal Preparation of Homogeneous Cobalt Oxide Nanomaterials as Stable Anodes for Superior Lithium Ion Batteries

A Simple Preparative Method for Porous Hollow-Ware Stacked Cobalt Oxides and Their Catalytic Properties

Evolution of cobalt hydroxide from 2D microplatelets to a 3D hierarchical structure mediated by precursor concentration

Facile hydrothermally grown cobalt oxide (Co 3 O 4 ) nanostructures and their electrochemical performances

Synthesis and Characterization of Regular Hexagonal Fe 3 O 4 Nanoplates

An efficient method for the preparation of magnetic Co3O4 nanoparticles and the study of their catalytic application

Ordered Arrays and Magnetic Properties of Cobalt Nanoparticles

Experimental and theoretical investigations on the hexagonal structure of Co2O3 nanoparticles synthesized via simple precipitation method

Preparation and catalytic properties of tungsten oxides with different morphologies

Cobalt-based coordination polymer-derived hexagonal porous cobalt oxide nanoplate as an enhanced catalyst for hydrogen generation from hydrolysis of borohydride

Hydrothermal Synthesis and Structure Evolution of Hierarchical Cobalt Sulfidenanostructures

Controllable hydrothermal-assisted synthesis of mesoporous Co3O4 nanosheets

Hydrothermal Synthesis, Characterization, and Electrochemical Behaviour of Cobalt Oxide (Co3O4) Nanoparticles for Stable Electrode with Enhanced Supercapacitance

Interface-mediated synthesis of transition-metal (Mn, Co, and Ni) hydroxide nanoplates

Soft-chemical exfoliation route to layered cobalt oxide monolayers and its application for film deposition and nanoparticle synthesis