Abstract:The as-cast and annealed Fe 76 Si 19.4 Nb 2.7 Cu 1.7 P 0.2 ribbons with width of 2.5 cm prepared by a single-roller cooling method were investigated. The structural properties of ribbons were studied by X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM). The XRD result shows the α-Fe crystal phase of annealed film. The average crystallite sizes of the as-cast and annealed ribbons are about 28 nm and 43 nm obtained from EF-SEM. The dielectric and magnetic properties of ribbons were tested over frequency ranges of 5 MHz to 300 MHz and 5 MHz to 3000 MHz using an Impedance Analyzer, respectively. The dielectric constant and dielectric loss of the as-cast ribbon decreases from 4.3 × 10 5 to 180 and from 3.01 to 0.06, while that of annealed ribbon decreases from 2.5 × 10 4 to 180 and from 3.01 to 1.31. The permeability decreased with increasing frequency at first of each ribbon and the value of annealed ribbon is bigger. It was observed that the permeability loss value of annealed ribbon is smaller at first and then bigger than that of as-cast ribbon. The smallest values of permeability of the as-cast and annealed ribbons are about 1.4 and 1.8. The minimum of the permeability loss of the as-cast ribbon is 0.008. The magnetic hysteresis loops were investigated using a vibrating sample magnetometer. The saturation magnetizations of the as-cast and annealed ribbons are 113 emu g −1 and 123 emu g −1 . The coercive fields of the as-cast and annealed ribbons are 259 A m −1 and 1130 A m −1 . The saturation magnetization and coercive field could become bigger due to the crystallize property.

High Permeability Nano-Crystalline FeSiBTaAg Ribbons Obtained by Direct Casting

Soft-Magnetic Fe-Based Nano-Crystalline Thick Ribbons

Crystallization kinetics and magnetic properties of Fe 63.5Co10Si13.5B9Cu 1Nb3 nanocrystalline powder cores

Crystallization Kinetics and Magnetic Properties of Fe73.5si13.5b9cu1nb1v2 Nanocrystalline Powder Cores

Crystallization Kinetics of Co-Finemet Amorphous Alloys and Magnetic Properties of Nanocrystalline Powder Cores

Magnetic properties of 120-mm wide ribbons of high Bs and low core-loss NANOMET® alloy

Magnetic properties and crystallization behavior of Fe-based nanocrystalline strips fabricated by twin-roll casting

Nanocrystalline Fe83Si4B10P2Cu1 ribbons with improved soft magnetic properties and bendability prepared via rapid annealing of the amorphous precursor

Effects of boron content on the structure and magnetic properties of Fe81-xSi13BxMo2Cr1Cu1P2 nanocrystalline alloys

Nanocrystallites Via Direct Melt Spinning of Fe77Ni5.5Co5.5Zr7B4Cu for Enhanced Magnetic Softness

Nanocrystalline Soft Magnetic Ribbon with Α″-Fe16n2 Nanocrystallites Embedded in Amorphous Matrix

Development of high Bs Fe–Ni-based metal amorphous nanocomposite by optimization of glass-forming ability

Effect of transverse magnetic field annealing on the magnetic properties and microstructure of FeSiBNbCuP nanocrystalline alloys

Study of dielectric and magnetic properties with Fe76Si19.4Nb2.7Cu1.7P0.2 ribbons

Production of Nanocrystalline (Fe, Co)-Si-B-P-Cu Alloy with Excellent Soft Magnetic Properties for Commercial Applications

Effects of Ribbon Thickness on Structure and Soft Magnetic Properties of a High-Cu-Content FeBCuNb Nanocrystalline Alloy

Fabrication of Fe-6.5wt%Si Ribbons by Melt Spinning Method on Large Scale

Characterisation of rapidly solidified nanocrystalline soft magnetic ribbons based on FeSiB with P and Ga additions

Soft magnetic properties and giant magneto-impedance effect of Co68.15Fe4.35Si12.5B15-Cr amorphous ribbons

Magnetic and structural behaviours of nanocrystalline Fe 70.8 Nb 3.7 Cu 1 Al 2.7 Mn 0.7 Si 13.5 B 7.6 alloy

Soft Magnetic Properties of Magnetic Cores Assembled With a High $B_{s}$ Fe-Based Nanocrystalline Alloy