Preparation and Protective Effects of Nano-Tio2 Composite Coatings on LY12 Aluminum Alloys

LI Heng,LI Cheng

DOI: https://doi.org/10.3969/j.issn.1007-791x.2011.01.010

2011-01-01

Abstract:To improve the corrosion resistance,nano-TiO2 composite coatings are prepared on the aluminum alloy substrates via the sol-gel process in which tetraethoxysilane(TEOS) is used as precursor,accompanied with-aminopropyltriethoxysilane(KH550) and some nano-TiO 2.HAc is added as catalyst in the sol-gel process to control the limited hydrolysis.Sols are coated on the surface of aluminum alloy substrates by dip-coating technique.Fluoroalkylsilane is used as dressing agent to surface of composite coatings.The results of electrochemical analysis show that the composite coatings with nano-TiO2 can improve the corrosion resistance of aluminium alloy substrates in 3.5%(mass ratio) NaCl solution effectively.When the sol contains 0.04% mass fraction of nanoTiO2,the corrosion current density for coated sample is 5.965×109 A/cm2,which is 4 orders of magnitude lower compared with that for bared sample(7.216×105 A/cm2).The scanning electron microscopy(SEM) and contact angle are measured to examine the compactness and hydrophobic nature of coatings.