Fabrication of Ti3C2Tx‐based superhydrophobic composite coating for reinforcement corrosion resistance of AZ31B Mg alloy
Xingxing Yin,Bingfeng Li,Shuaiya Xue,Peng Mu,Jian Li
DOI: https://doi.org/10.1002/adem.202201573
IF: 3.6
2022-12-18
Advanced Engineering Materials
Abstract:Incorporating MXene nanomaterials in coating is an effective strategy to fabricate anticorrosive coatings with superior corrosion resistance, depending on its characteristic structure and nature. However, it may accelerate the corrosion rate of metal once forming galvanic corrosion by direct contact with the substrate due to its high conductivity and hydrophilicity. Herein, we used 1H, 1H, 2H, 2H‐Perfluorodecyltrichlorosilane (PFDTS) to functionalize Ti3C2Tx nanosheets to obtain superhydrophobic Ti3C2Tx hybrids, which greatly enhances the hydrophobicity of Ti3C2Tx nanosheets. Then a new strategy was designed to construct superhydrophobic Ti3C2Tx/epoxy/cerium conversion (STECC) composite coating with sandwich‐like structure, which consisted of bottom cerium conversion coating, intermediate epoxy coating and top superhydrophobic Ti3C2Tx coating layer. The underlying cerium conversion layer and intermediate epoxy coating acted as the protective coating not only improve the corrosion protection ability of substrate but also isolate the top superhydrophobic Ti3C2Tx layer from direct contact with the substrate, which could eliminate direct contact between MXene and Mg alloy to further restrain the corrosion‐promotion effect of Ti3C2Tx. The STECC with unique structure exhibited excellent water repellency with water contact angle of 155.8° and sliding angle of 5°, which endowed the metal substrate with outstanding antifouling property. Moreover, the STECC composite coating illustrated robust mechanical and chemical stability. Electrochemical experimental results demonstrated that the modified MXene nanosheets could remarkably improve the corrosion protection performance of STECC composite coating, and the corrosion current density decreased from 5.905 × 10‐3 A⋅cm‐2 of bare substrate to 3.602 × 10‐8 A⋅cm‐2 of the coated specimen. Moreover, the impedance modulus of STECC coating reached the value of approximately 7.49 ×106 Ω·cm2 and increased 4 orders of magnitude compared with the Mg substrate, indicating the excellent anticorrosion property of the STECC coating. The composite coating studied here may offer valuable insights and inspiration toward developing MXene‐based coating for high‐performance anticorrosion. This article is protected by copyright. All rights reserved.
materials science, multidisciplinary