Microstructure and Corrosion Resistance of Modified 2024 Al Alloy Using Surface Mechanical Attrition Treatment Combined with Microarc Oxidation Process

Lei Wen,Yaming Wang,Yu Zhou,Lixin Guo,Jia-Hu Ouyang
DOI: https://doi.org/10.1016/j.corsci.2010.09.061
IF: 7.72
2011-01-01
Corrosion Science
Abstract:A top ceramic coating was fabricated on the surface mechanical attrition treatment (SMAT) modified nanocrystalline layer of 2024 Al alloy by microarc oxidation (MAO) process. The corrosion resistance of the SMAT-MAO composite coating was studied by EIS. The results show that SMAT-MAO composite coating with 10μm top ceramic coating exhibited better corrosion resistance, while the SMAT-MAO coating with the thickness of 15μm showed worse corrosion resistance compared with those simple MAO coatings with same thickness. The formation of a dense passive film at the damaged region caused by the bottom nanocrystalline interface contributed to the improved corrosion resistance property.