Study on the wear resistance and corrosion behaviour of self-sealed MAO/ZrO 2 coatings prepared on 7075 aluminium alloy

Xing Qi,Jun Li,Yafeng He,Yuntong Liu,Rui Liu,Renguo Song

DOI: https://doi.org/10.1016/j.jallcom.2023.172436

IF: 6.2

2023-10-16

Journal of Alloys and Compounds

Abstract:Self-sealed microarc oxidation (MAO) coatings were prepared on 7075 aluminium alloy by incorporating different concentrations of ZrO 2 particles. The wear resistance and corrosion behaviour of MAO- and MAO/ZrO 2 -coated alloys were investigated. The results show that the tribological behaviour of the coatings was controlled by an abrasive mechanism. The coefficient of friction (COF) for the MAO/ZrO 2 -coated samples decreased to 0.82, indicating that the wear resistance was significantly improved due to the incorporation of hard ZrO 2 particles and the enhanced compactness and surface roughness of the coatings. The sealed pores effectively prevented the permeation of the corrosion solution, thus increasing the electrochemical corrosion resistance . Pores and microcracks would be enlarged and preferentially fractured during slow strain rate testing (SSRT) and thus were the initial sites for corrosion pitting and SCC crack propagation. The interlocking mechanism between the pores (microcracks) and ZrO 2 particles enhanced the strength of the pores (microcracks); therefore, the stress corrosion cracking (SCC) susceptibility of the MAO/ZrO 2 -coated samples was also reduced. Moreover, the MAO/ZrO 2 coatings formed with the addition of 4 g/L ZrO 2 particles had the best corrosion resistance, and the SCC susceptibility was reduced by 8.1% compared with that of the Al matrix.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering