Corrosion Behavior of Novolac Epoxy Coated Tinplate System in Energy Drink

Xia Dahai,Wang Jihui,Jiang Yuxuan,Li Na,Zhou Chao

DOI: https://doi.org/10.11784/tdxb20130606

2013-01-01

Abstract:The corrosion process of novolac epoxy coated tinplate system in energy drink was investigated by using electrochemical impedance spectroscopy(EIS) and electrochemical noise(EN) techniques,and the corrosion mechanism was discussed based on the surface characterization by scanning electron microscopy(SEM) and energy dispersive X-ray spectroscopy(EDS).The results show that in the first 3 days there was only one time-constant in EIS plot,indicating that the organic coating had good protective performance.After 28 days’ corrosion,EIS plots showed 2 time-constants,indicating that the electrolyte had permeated through the organic coating.There were 3 time-constants in the EIS plots after 220 days’ corrosion,indicating that corrosion had occurred on the tinplate.One time-constant was seen in EIS plots after 364 days’ corrosion,indicating that the organic coating had basically lost its protective performance.The amplitude of current noise increased as time got prolonged,which indicated that the corrosion of the substrate metal was more and more serious.The entire deterioration process of novolac epoxy coated tinplate system in energy drink could be divided into three main stages.Stage I was the wetting of organic coating,stage Ⅱ was the corrosion initiation beneath the coating,and stage Ⅲ was the corrosion extension.The corrosion mechanism was firstly the damage of organic coating and the formation of micropores during the corrosion process,and then the disso-lution of tinplate under the organic coating.After the tinplate was corroded,the carbon steel substrate started to dissolve and became the dominated corrosion process due to its higher electrochemical activity.