EIS STUDY ON THE DETERIORATION PROCESS OF ORGANIC COATINGS UNDER IMMERSION AND CYCLIC WET-DRY CONDITIONS

张伟,王佳,赵增元,刘学庆

2011-01-01

Abstract:Comparing between immersed and cyclic wet-dry conditions,the deterioration processes of the organic coatings on carbon steel surface have been comparatively studied by using electrochemical impedance spectroscopy（EIS）.The wet-dry cycles were carried out in the alternating conditions by immersing in a 3.5% sodium chloride solution and drying at 25°and 50%RH for 4 h respectively.Coating resistance,R_f,coating capacitance,Cf,and double layer capacitance,Cd,were monitored continuously and separately under above two conditions.The percentages of the interface active area,A_w,were estimated from the obtained double layer capacitance,C_d.According to the EIS characteristics,the entire deterioration processes under two above-mentioned conditions can be divided into three main stages,consisting of the medium penetration into coatings, corrosion initiation and corrosion extension underlying coatings. In comparison with the immersed,the wet-dry cycles greatly accelerated the entire deterioration process; especially the corrosion initiation and the corrosion extension periods,leading the paint system lose its anti-corrosive performance in a short period.However,the underlying substrate corrosion of the cyclic coatings was far less serious than the immersed;even the delaminating area was seven times more than the immersed. The acceleration mechanism of the coatings and underlying metal corrosion under wet-dry cycles was discussed based on the above results.