Abstract:The system Y 1−x Sr x MnO 3 (x = 0.000, 0.005, 0.010, 0.050, and 0.100) was studied as a potential cathode material for solid oxide fuel cells. Powders were prepared using an organometallic precursor; however, achieving homogeneous compositions was complicated due to the presence of intermediate, metastable phases. The desired hexagonal Y 1−x Sr x MnO 3 phase formed from the precursor at 800 °C, while small amounts of a metastable orthorhombic (Y,Sr)MnO 3 phase formed in the temperature range between 850°and 960 °C, and another orthorhombic YMn 2 O 5 phase between 840°and 1200 °C. The metastable (Y, Sr)MnO 3 phase readily transformed into the stable hexagonal phase at about 960 °C. The other metastable intermediate phase, YMn 2 O 5 , was formed as a decomposition product of a portion of the major hexagonal YMnO 3 at 840 °C, and subsequently reacted with Y 2 O 3 back to the hexagonal YMnO 3 at 1200 °C. For the studied compositions, densities higher than 95% theoretical could be obtained by sintering in air at temperatures above 1400 °C for 2 h. The investigated system was comparable in electrical conductivity with the current cathode material La 1−x Sr x MnO 3 , and had an average apparent thermal expansion coefficient between 5 and 7 ppm/°C in the temperature range between 200°and 1000 °C. Unfortunately microcracking was observed in all sintered specimens, possibly caused by a high-temperature phase transition between the hexagonal and cubic polymorphs of Y 1−x Sr x MnO 3 . The microcracking presents a major obstacle to the use of this material as a cathode in solid oxide fuel cells.

Sintering Properties of La1-xSrxMnO3 Prepared by SHS

Preparation and Characterization of Porous La1-xSrxMnO3

Preparation and Properties of Cathode Materials for SOFC

Study on the Cathodes Material La 1- X Sr X MnO 3 for SOFC

Properties of nonstoichiometric Pr0.6-xSr0.4MnO3 as the cathodes of SOFCs

Solid State Reactive Mechanism of La1-xSrxMnO3

A Study of (pr, Nd, Sm)1−xSrxMnO3 Cathode Materials for Solid Oxide Fuel Cell

Improvement of Electromagnetic Properties at Room Temperature in La0.625Ca0.375-Sr MnO3:Ag0.2 (x = 0.09–0.15) Ceramics by Sr Doping

Preparation and characterization of La1−xSrxNiyFe1−yO3−δ cathodes for low-temperature solid oxide fuel cells

Synthesis and properties of strontium-doped yttrium manganite

Low-temperature solid oxide fuel cells with La1-xSrxMnO3 as the cathodes

Synthesis and Characterization of SmSrCo2−xMnxO5+δ (x=0.0, 0.2, 0.4, 0.6, 0.8, 1.0) Cathode Materials for Intermediate-Temperature Solid-Oxide Fuel Cells

Electrochemical Characteristics of Solid Oxide Fuel Cell Cathodes Prepared by Infiltrating (la,sr)mno3 Nanoparticles into Yttria-Stabilized Bismuth Oxide Backbones

New Electrode of La<sub>0.75</sub>Sr<sub>0.25</sub>Mn<sub>0.5</sub>Cr<sub>0.5-X</sub>Cu<sub>x</sub>O<sub>3-δ</sub> (x=0, 0.05, 0.10, 0.20) for Symmetric Solid Oxide Fuel Cell

Investigation of structural, electrical and electrochemical properties of La0.8Sr0.2Mn1−xScxO3−δ as cathode on yttria-stabilized zirconia electrolyte for intermediate temperature solid oxide fuel cell fabricated by one step dry pressing method

Microstructure and Electrochemical Behavior of La0.8Sr0.2MnO3 Deposited by Solution Precursor Plasma Spraying

Investigation of structural, electrical and electrochemical properties of La0.6Sr0.4Fe0.8Mn0.2O3-δ as an intermediate temperature solid oxide fuel cell cathode

Preparation and Characterization of Pr1−xSrxFeO3 Cathode Material for Intermediate Temperature Solid Oxide Fuel Cells

Synthesis and Properties of Pr1-xSrxAlO3-δ as Cathode of Solid Oxide Fuel Cells

Synthesis and Characterization of La_(0.75)Sr_(0.25)Mn_(0.5)Cr_(0.5-x)Cu_xO_(3-δ) for SOFC Anode Material

Preparation, Structure and Performance of La0.6Sr0.4Co0.2Fe0.8O3 Cathodes of Intermediate Temperature Solid Oxide Fuel Cells