Dielectric and piezoelectric properties of acrylonitrile butadiene rubber/lead magnesio-niobate piezoelectric ceram/carbon fiber composites

Liu Li,Liu Yandong,Cao Jianli,Zhang Liqun

DOI: https://doi.org/10.3969/j.issn.1000-1255.2007.03.008

2007-01-01

Abstract:A new composite with special piezoelectric property was prepared by using lead magnesio-niobate piezoelectric ceramic powders (PMN) as dispersing phase and carbon fiber (CF) as electric-conducting filler in acrylonitrile butadiene rubber (NBR) matrix. The dielectric and piezoelectric properties of the composites were studied. The results showed that particle size of 80% of PMN ceramic powders was 0.5～2.0 μm, and the packed density of PMN was 6.6 g/cm3. When volume fraction of CF was less than 5%, the content of CF had no effect on breakdown voltages of the composites. When volume fraction of CF was 10%, the breakdown voltage of the composite was decreased to 1/3~1/2 of that of the composite without CF. The piezoelectric constant (d33) of the composite increased with increasing the volume fraction of PMN, and appropriate delay of polarizing time or increasing polarizing voltage could be helpful to improve the value of d33. The optimal polarzing voltage was 7 kV/mm and the optimal polarzing time was 25 min. The dielectric constant (ε) increased with the increasing the volume contents of PMN. When the volume fraction of CF was 0, the change trend of ε and dielectric dissipation factor(tan δ) of the composites was opposite. When the volume fraction of CF was 5%, the ε and tan δ of the composites increased instead.