Morphology and Permeability of Ipp Hollow Fiber Membrane Via Thermally Induced Phase Separation after Stretching

LI Pingli,HUANG Hui,ZHOU Lei,WU Haoyun,CHANG Heying,WANG Shichang

DOI: https://doi.org/10.3969/j.issn.1007-8924.2012.06.002

2012-01-01

Abstract:By melting and blending isotactic polypropylene(iPP)/di-n-butyl phthalate(DBP)/ dioctyl phthalate(DOP) system,iPP hollow fiber membrane was prepared via thermally induced phase separation(TIPS) method.Subsequently,the hollow fiber membranes were stretched at different stretching temperature and stretching ratio.The membrane structure and permeability were characterized.The cortex on the outer surface of the membrane and the membrane structure have been made better,which were observed with environmental scanning electron microscope.The tensile strength of hollow fiber membrane was tested by electronic universal testing machine.The porosity,the pure water flux and the tensile strength of the membrane increase firstly and then decrease,with increasing stretching temperature and stretching ratio.The porosity increases by 35.3%,the pure water flux of the membrane raises by 286.9% and the tensile strength can increases to 6.86 MPa.The performance of the hybrid membrane which was added with nano-SiO2 after the stretching is improved:the porosity raises by 46.8%,the pure water flux increases by 416.1% and the tensile strength can raise by 181.9%.It is suggested that the cortex on the outer surface and the permeability of the membrane can be made better by stretch processing which can optimize the membrane structure.