Abstract:We report on intense red fluorescence from Mn(2+)-doped sulfophosphate glasses and glass ceramics of the type ZnO-Na(2)O-SO(3)-P(2)O(5). As a hypothesis, controlled internal crystallization of as-melted glasses is achieved on the basis of thermally-induced bimodal separation of an SO(3)-rich phase. Crystal formation is then confined to the relict structure of phase separation. The whole synthesis procedure is performed in air at <or= 800 degrees C. Electron spin resonance and Raman spectroscopy indicate that Mn(2+) species are incorporated on Zn(2+) sites with increasingly ionic character for increasing concentration. Correspondingly, in the glasses, increasing MnO content results in decreasing network polymerization. Stable glasses and continuously increasing emission intensity are observed for relatively high dopant concentration of up to 3 mol.%. Recrystallization of the glass results in strongly increasing emission intensity. Dynamic emission spectroscopy reveals only on type of emission centers in the glassy material, whereas three different centers are observed in the glass ceramic. These are attributed to octahedrally coordinated Mn(2+) in the residual glass phase and in crystalline phosphate and sulfate lattices, respectively. Relatively low crystal field strength results in almost ideal red emission, peaking around 625 nm. Excitation bands lie in the blue-to-green spectral range and exhibit strong overlap. The optimum excitation range matches the emission properties of GaN- and InGaN-based light emitting devices.

Photo-stimulated Long-Lasting Phosphorescence in Mn2+-doped Zinc Borosilicate Glasses

Long Lasting Phosphorescence in Mn2+-Activeted ZnO-B2O3 Glass

Multi-color long-lasting phosphorescence in Mn2+-doped ZnO–B2O3–SiO2 glass–ceramics

Red Long Lasting Phosphorescence of Mn~(2+) Doped Zinc Phosphate Glasses

Long Lasting Phosphorescence and Photo-Stimulated Long Lasting Phosphorescence in Tb~(3+)-doped Strontium Borosilicate Glasses

Photoluminescence and Afterglow of Mn2+ Doped Lithium Zinc Silicate

Sol-gel preparation and phosphorescence property of Mn 2+ -doped zinc borosilicate glass thin films

Long Lasting Phosphorescence, Thermoluminescence and Electron Spin Resonance Property of Mn2+ Activated Zno-Al2o3sio2 Ceramic

Near Infrared Long Lasting Emission of Yb3+ and Its Influence on the Optical Storage Ability of Mn2+-Activated Zinc Borosilicate Glasses

Infrared Femtosecond Laser Induced Visible Long-Lasting Phosphorescence in Mn2+-Doped Sodium Borate Glasses

Blue and red long lasting phosphorescence (LLP) in β-Zn(PO):Mn,Zr

Long-lasting Luminescence Properties of ZnO-B2O3:Tb3+

Effect of Network-Forming Oxides on Long-Lasting Phosphorescencein Mn2+ Doped ZnO-B2O3-SiO2 Glass

Blue And Red Long Lasting Phosphorescence (Llp) In Beta-Zn-3(Po4)(2): Mn2+ Zr-,(4+)

Preparation of long-lasting phosphorescence (LLP) glass-ceramic materials

Long Persistent Luminescence in Mn^2+-activated Sodium Gallium Germanate Glass and Glass Ceramics Induced by Infrared Femtosecond Laser Pulses

Femtosecond Laser-Induced Long-Lasting Phosphorescence In Pr3+-Doped Zno-B2o3-Sio2 Glass

The role of excess Zn2+ ions in improvement of red long lasting phosphorescence (LLP) performance of β-Zn3(PO4)2:Mn phosphor

Long lasting phosphorescence of Eu2+ in reduced SrO–B2O3 glasses

Intense Red Photoluminescence from Mn2+-doped (na+; Zn2+) Sulfophosphate Glasses and Glass Ceramics As LED Converters.

Long lasting phosphorescence of Eu~(2+)-activated MO-B_2O_3 glasses