Blue and red long lasting phosphorescence (LLP) in β-Zn(PO):Mn,Zr

J WANG,Q SU,S WANG
DOI: https://doi.org/10.1016/j.jpcs.2005.03.006
IF: 4.383
2005-01-01
Journal of Physics and Chemistry of Solids
Abstract:Multi-color long lasting phosphorescent (LLP) phenomenon in β-Zn3(PO4)2:Mn2+,Zr4+ was systematically investigated. It is found that the red (λEm=616nm) LLP performance of Mn2+ such as brightness and duration is largely improved, and that the blue (λEm=475nm) LLP of Zr4+ with lower intensity appears when Zr4+ ions are co-doped into the matrix. The fluorescence, phosphorescence and thermoluminescence (TL) spectra show that Mn2+ ion is solely expected as a luminescent center, while Zr4+ ion not only acts as a luminescent center, but also induces an electron trap (TrapZr) associated with a TL peak at 344K. The trap depth for TrapZr is 0.25eV, while that for the intrinsic trap is 0.38eV, associated with a dominant peak at 385K for Zn3(PO4)2:Mn2+. The Zr4+-induced trap with suitable depth is responsible for the improvement of the red LLP of Mn2+ ion and the appearance of the blue LLP of Zr4+ ion. The LLP mechanism is also investigated.
What problem does this paper attempt to address?