Abstract:Novel red long-lasting phosphorescent materials beta-Zn-3(PO4)(2): Mn2+, M3+ (M = Al and Ga) were synthesized by means of high-temperature solid-state reaction. Photoluminescence (PL) excitation and emission, long-lasting phosphorescent (LLP) emission, decay curves, brightness and chromaticity coordination, and thermostimulated-luminescent (TSL) spectra were used to characterize the powder phosphors. The emissions for both PL and LLP are due to the T-4(1g)((4)G) --> (6)A(1g)(S-6) transition of Mn2+ ions in beta-Zn-3(PO4)(2). The incorporation of trivalent ions M 31 decreases the PL intensity and contrarily improves the LLP properties including brightness and duration with increasing ionic radius. After irradiation with ultraviolet light peaking at 254 nm, Zn-3(PO4)(2): Mn2+, Ga3+ shows the initial intensity of the red phosphorescence at 460 mcd m(-2) with the chromaticity coordinates x = 0.6679, y = 0.3321 after the removal of the excitation source. Its red phosphorescence lasts no less than 2.5 h. The results of TSL show that some intrinsic defects associated with peaks at 381, 450 and 510 K appear in Zn-3(PO4)(2): Mn2+ whereas a novel compensating defect V-Zn" for the substitution of Zn2+ by Al3+ and Ga3+ is associated with peaks at 380 K for Zn-3(PO4)(2): Mn2+, Al3+ and 377 K for Zn-3(PO4)(2): Mn2+, Ga3+. The negative defect V-Zn" serves as an efficient hole-trapping center. The density of the trapped-charges for the TSL peaks at 380 and 377 K is respectively 1.2 and 2.7 times more intensive than that for the peak at 381 K. The TSL intensity is strongly dependent on the density of the trapped charges. An electron - hole recombination model is proposed to interpret the mechanism for the red LLP of Mn2+. Based on this model, the improvement of red LLP performance of Mn2+ is strongly related to the density of the trapped charges, which can be modified by the added ions. It demonstrates that the red LLP performance of Mn2+ can be controlled by the species of the auxiliary ions.

The role of excess Zn2+ ions in improvement of red long lasting phosphorescence (LLP) performance of β-Zn3(PO4)2:Mn phosphor

Blue and red long lasting phosphorescence (LLP) in β-Zn(PO):Mn,Zr

Blue And Red Long Lasting Phosphorescence (Llp) In Beta-Zn-3(Po4)(2): Mn2+ Zr-,(4+)

Phosphorescence properties and energy transfer of red long-lasting phosphorescent (LLP) material β-Zn3(PO4)2:Mn2+,Pr3+

A novel red long lasting phosphorescent (LLP) material β-Zn3(PO4)2:Mn2+, Sm3+

Synthesis, Photoluminescence and Thermostimulated-Luminescence Properties of Novel Red Long-Lasting Phosphorescent Materials Β-Zn3(po4)2:Mn2+,m3+(m = Al and Ga)

Long Lasting Phosphorescent Properties of Β-Zn3(po4)2∶mn2+,b3+ Materials

Red Long Lasting Phosphorescence of Mn~(2+) Doped Zinc Phosphate Glasses

Long Lasting Phosphorescence in Mn2+-Activeted ZnO-B2O3 Glass

Defects Enhanced Photoluminescence of Mn2+-doped ZrP2O7 Blue LLP Materials

Insight into a Novel Rare-Earth-free Red-Emitting Phosphor Li3Mg2NbO6:Mn4+: Structure and Luminescence Properties

Role of Intrinsic Defects on the Persistent Luminescence of Pristine and Mn Doped ZnGa2O4

Effects of oxygen vacancies on luminescent properties of green long-lasting phosphorescent (LLP) material α-Zn 3 (PO 4 ) 2 : Mn 2+ , K +

Defect‐Induced Self‐Reduction and Anti‐Thermal Quenching in NaZn(PO 3 ) 3 :Mn 2+ Red Phosphor

Luminescence Performance and Vibronic Behavior of Mn4+-activated Ca14-xKxAl10Zn6O35 Deep-Red Phosphor.

Defect‐Induced Self‐Reduction and Anti‐Thermal Quenching in NaZn(PO3)3:Mn2+ Red Phosphor

Photostimulated Red Long-Lasting Phosphorescence In Beta-Zn-3 (Po4)(2): Mn2+,Ga3+

Phosphorescence behavior and photoluminescence mechanism of Dy 3+ sensitized β-Zn 3 (PO 4 ) 2 : Mn 2+ phosphor

Tunable Long Lasting Phosphorescence Due to the Selective Energy Transfer from Defects to Luminescent Centres Via Tunnelling in Mn(2+) and Tm(3+) Co-Doped Zinc Pyrophosphate.

Luminescence properties and the thermal quenching mechanism of Mn 2+ doped Zn 2 GeO 4 long persistent phosphors.

Adjusting luminescence properties of ZnAl2O4:Mn2+(Mn4+), Li+ phosphors through cation substitution