Abstract:ZnO nanocrystals doped transparent glass and glass-ceramics with visible emissions were successfully synthesized through melt-quenching method. Structures and defect-related photoluminescence of quenched glasses and glass-ceramics were significantly dependent on ZnO content in precursor and post heat treatment time. Nano-sized ZnO crystals could generate in quenched glass before heat treatment with a particular precursor composition (44SiO(2)-11Al(2)O(3)-40ZnO-10K(2)O, mol%), and this quenched glass emitted strong green emission. For glass-ceramics, short time (5 min) heat treatment was conducive to intensive green or yellow emission depending on the excitation energy. Further extending of heat treatment resulted in yellow emission as the dominant one, together with a decline of intensity due to reduced defects. Moreover, the emission peaks shifted towards longer wavelength, from violet, blue, to green and yellow, with an increase of heat treatment time, which can be ascribed to different defect states along with crystal growth during heat treatment. Green light corresponded to oxygen vacancies (V-0), the main defect of ZnO before heat treatment, whereas yellow light was associated with the transition from zinc interstitials (Zn-i) to oxygen interstitials (O-i) produced with the structure transformation during heat treatment. Yellow emission can emit with both above- and below-bandgap excitation, and preferentially excited by energy (395 nm, similar to 3.14 eV) below the bandgap, near Zn-i level. Green emission was only efficient under the excitation larger than bandgap. Defect-based mechanisms of visible emissions with different initial states were proposed. (C) 2018 Elsevier B.V. All rights reserved.

Femtosecond Laser-Induced Long-Lasting Phosphorescence In Pr3+-Doped Zno-B2o3-Sio2 Glass

Photostimulated Long-lasting Phosphorescence in Rare-earth-doped Glasses

Infrared Femtosecond Laser Induced Visible Long-Lasting Phosphorescence in Mn2+-Doped Sodium Borate Glasses

Femtosecond Laser-Induced Three-Dimensional Bright and Long-Lasting Phosphorescence Inside Calcium Aluminosilicate Glasses Doped with Rare Earth Ions

Long-lasting Phosphorescence and Photostimulated Long-Lasting Phosphorescence in Mn 2+ -Doped Alumino-Phosphofluoride Glasses Irradiated by a Femtosecond Laser

Long lasting phosphorescence in oxygen-deficient zinc–boron-germanosilicate glass–ceramics

Long-lasting Phosphorescence in Oxygen-Deficient Ge-doped Silica Glasses at Room Temperature

Study on Long-Lasting Phosphorescent Mechanism of Tb~(3+) Doped ZnO-B_2O_3-SiO_2 Glass

Intense O + E + S-band emission from Pr^3+-doped ZnF_2-based glasses

Near-infrared Emission of Yb3+ Through Energy Transfer from ZnO to Yb3+ in Glass Ceramic Containing ZnO Nanocrystals.

Phosphorescence and Photon-Stimulated Phosphorescence in Mn2+ Doped Alumino-Phosphofluoride Glass Irradiated by Femtosecond Laser

Fabrication and Visible Emissions of ZnO Nanocrystal Doped Transparent Zinc Silicate Glass-Ceramics

Up-conversion luminescence and near infrared luminescence of Er3+ in transparent oxyfluoride glass-ceramics

Orange-red upconversion luminescence of Sm3+ doped ZnO-B 2O3-SiO2 glass by infrared femtosecond laser irradiation

Rare-Earth Glasses for New Optical Applications - Microscopic Modifications by A Femtosecond Laser and Realization of New Optical Functions

Femtosecond laser induced color-center in phosphate glasses

Infrared femtosecond laser pulse-induced three-dimensional bright and long-lasting phosphorescence in a Ce3+-doped Ca2Al2SiO7 crystal

Micro-modification of luminescence property in Ag+-doped phosphate glass using femtosecond laser irradiation

Infrared femtosecond laser pulse-induced three-dimensional bright and long-lasting phosphorescence in a Ce^3+-doped Ca_2Al_2SiO_7 crystal

Nanoarchitectonics and spectroscopic studies of Pr3+ doped ZnS nanoparticles glasses for visible reddish orange luminescent device applications