Analysis of Surface and Sub-Surface of Cold-Rolled Al Plate Lubricated with Water-or Oil-Based Lubricants
XiWen Tang,ChenHui Zhang,Yan Wang,Ye Yang,Juan Hu
DOI: https://doi.org/10.1007/s11431-017-9075-2
2017-01-01
Science China Technological Sciences
Abstract:For environmental protection,energy conservation,and other reasons,water-based lubricants are increasingly chosen to replace oil lubricants.Water-based lubricants are divided into emulsified and solution types.Solution type water-based lubricants have attracted significant attention for the good stability,easy biodegradability,and safety for workers.However,some problems exist with current solution type water-based lubricants,such as poor lubricity and corrosion resistance.During the cold-rolling process,Al plate rolled using oil-based lubricant lubrication shows metallic luster,but that rolled using water-based lubricant shows corrosion spots,black strips,and no metallic luster.Therefore,this study mainly analyzed the reasons for the darkness of Al plate cold-rolled with water solution lubricants.The differences in plate surfaces lubricated by water solution and oil were investigated by scanning electron microscopy,auger electron spectroscopy,X-ray photoelectron spectroscopy,and transmission electron microscopy.The analysis results showed that the surface of the oil-lubricated sample is smooth,the oxygen content is low,and the oxide layer is thin,while the surface of the water solution-lubricated sample is rough,the oxygen content is high,the chemical composition is more complex,and the oxide layer is not uniform and thick.