Abstract:Organosoluble polyimide/silica hybrid materials were prepared via the sol–gel process and their pervaporation properties were studied. The organosoluble polyimide (PI) was based on 4,4′-oxydiphthlic dianhydride (ODPA) and 4,4′-diamino-3,3′-dimethyldiphenylmethane (DMMDA). The surface chemical structure of polyimide/silica films was analyzed by Fourier transform infrared (FT-IR) and X-ray photoelectron spectroscopy (XPS) and the results show that the completely hydrolysis of alkoxy groups of precursors and formation of the three-dimensional Si–O–Si network in the hybrid films. The morphology and the silica domain thus obtained were studied by scanning electron microscopy (SEM) and atomic force microscopy (AFM), respectively. The silica particle size in the hybrid is in the range of 40–100nm for the hybrid films when the amount of silica is less than 20wt%. The strength and the modulus of the hybrid films are improved and the mechanical properties were found to be strongly dependent on the density of the crosslink. The glass transition temperature (Tg) of the hybrid films was determined by dynamic mechanical analysis (DMA) and the value increased 15–20°C as the silica content increased. Furthermore, the pervaporation performances of the prepared hybrid films were also investigated for the ethanol/water mixtures at different temperature.

A Study on PTFE/SiO2 Hybrid Film Made by the Sol-gel

PREPARATION AND STUDY ON STRUCTURE OF THE POLYIMIDE/SILICA HYBRID AND NANOCOMPOSITE FILMS

Preparation and Research of Hydrophobic PDMS/Nano-SiO2 Modified SiO2 Coating

Preparation and Thermal Stability of Polyorganosiloxane Superhydrophobic Film by Sol-Gel Method

A Technical to Increase Thickness of Resin Film Avoiding Cracking

Investigation on the Microstructure and Optical Performance of TiO_2 Films by Sol-Gel Method

Facile preparation of super-hydrophobic and super-oleophilic silica film on stainless steel mesh via sol–gel process

Microstructure and Properties of Organosoluble Polyimide/silica Hybrid Films

Structure and Photocatalytic Properties of TiO2/Perfluorosulfonated Resin Hybrid Films Prepared by Sol-Gel Method

Influence of water contents on structure and properties of SiO 2-PEDT composite antistatic thin film by sol-gel process

Study of Self-Cleaning and Low-Emission Properties of FTO/TiO2 Composite films

Preparation of SiO2-PEDT composite antistatic film by sol-gel method

Study of silicon-based ferroelectric PZT thin films fabricated by sol-gel method

Preparation and Properties of Superhydrophobic Fluoroalkylsilane Coatings

Achieving durable hydrophilic modification of polytetrafluoroethylene (PTFE) through organic/inorganic hybridization strategy

An Efficient Way to Prepare Hydrophobic Antireflective SiO2 Film by Sol–gel Method

Preparation of Zirconia/Organosilicone Thin Film by Sol-Gel Method

Preparation and Effect Factors of TiO2 Superhydrophobic Coating

Study of silicon-based ferroelectric thin films prepared by Sol-Gel method

Study on the cracking of SiO2-TiO2 films prepared by sol-gel method

Water-repellent hierarchical microstructured PTFE films via micro powder hot embossing