Preparation of SiO2-PEDT composite antistatic film by sol-gel method

Chunchun Wu,Xingeng Ding,Fang'er Yang,Lu Wenwei

2004-01-01

Rare Metal Materials and Engineering

Abstract:The SiO2-PEDT composite antistatic film was prepared by sol-gel method. The surface morphology of the film was investigated by SEM, and the properties of the electric conductivity and the optic of the film were studied by a surface resistance meter and spectrophotometer. The result indicated that the viscosity of composite sol increased linearly with increasing of water (R); the time of gelation shortened dramatically and the optimal amount of water was 2; PEDT conductive particles were well dispersed in the film, when the mount of PEDT sol was below 5.08wt%, the resistance of film still remained in 10(10)&UOmega;/□ with increasing of PEDT. When the amount of PEDT lied between 5.08wt% and 7.44wt%, the resistance decreased rapidly from 8 X 10(10)&UOmega;/□ 0 to 8 X 10(8)&UOmega;/□. The mechanism of conductivity belonged to the effect of channel for electric conductinge. When the amount was more than 7.44wt%, resistance decreased from 8 X 10(8)&UOmega;/□ to 7.2 X 10(7)&UOmega;/□. Upon increasing amount of PEDT, the transmittance of the film decreased from 99.8% to 94.2% gradually, and the adhesion of film got worse.