Abstract:Conductive Poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) has been extensively used as non-metallic electrodes. However, the relatively low electrical conductivity of pristine PEDOT:PSS film restricts its further application. Although doping high content conductive filler or increasing the film thickness are effective for enhancing the electrical property, the transparency is sacrificed, which limits the application of PEDOT:PSS films. In this study, preparing PEDOT:PSS composite film with highly conductive and transparent property was the primary purpose. To achieve this goal, single-walled carbon nanotubes (SWCNTs) and dimethyl sulfoxide (DMSO) was chosen to composite with PEDOT:PSS. The spin-coated SWCNT/PEDOT:PSS composite film exhibited excellent electrical conductivity and transparency. The electrical conductivity of composite film with desired transmittance property (78%) reached the highest value (1060.96 S cm(-1)) at the SWCNTs content was 6 wt%. Under the modification process applied in this work, the non-conductive PSS was partially removed by incorporated DMSO and SWCNTs. Then, the molecular chains of PEDOT stretched and adsorbed onto the surface of SWCNTs, forming a highly efficient three-dimensional conductive structure, which contributed to the enhancement of electrical conductivity and transparency. Additionally, the spin-coating process allowed for the reduction of film thickness, ensuring better transparency. This research contributed to expanding the further applications of PEDOT:PSS films in high-performance transparent film electrodes.

Incorporation of Single-Walled Carbon Nanotubes with PEDOT/PSS in DMSO for the Production of Transparent Conducting Films

Spin Coated Ultrathin PEDOT:PSS/SWCNT Film with High Electronic Conductivity

Improved Resistance Stability of Transparent Conducting Films Prepared by PEDOT: PSS Hybrid CNTs Treated by a Two-Step Method

Carbon nanotube transparent conducting films as electrodes for organic light-emitting diodes

Induced electrical polarization and conductivity homogenization via internal architectural regulation in PC/PVDF/MWCNTs/PEDOT:PSS transparent conductive films

Highly conductive sandwich-structured CNT/PEDOT:PSS/CNT transparent conductive films for OLED electrodes

Dispersion of Single-Walled Carbon Nanotubes by Nafion in Water/Ethanol for Preparing Transparent Conducting Films

Flexible, Highly Transparent, and Conductive Poly(3,4-ethylenedioxythiophene)-Polypropylene Composite Films of Nanofibrillar Morphology

High-Performance Transparent PEDOT: PSS/CNT Films for OLEDs

Modification of carbon nanotube transparent conducting films for electrodes in organic light-emitting diodes

Stable Doping of Single-Walled Carbon Nanotubes for Flexible Transparent Conductive Films

Cooperative Effect of Carbon Nanotubes and Dimethyl Sulfoxide on PEDOT: PSS Hole Transport Layer in Planar Perovskite Solar Cells

A Comprehensive Study of Sulfonated Carbon Materials As Conductive Composites for Polymer Solar Cells

A Solution Processable Flexible Transparent Conductive Graphene/PEDOT: PSS Film Fabricated by Spin and Blade Coating

Solution-processed metallic conducting polymer films as transparent electrode of optoelectronic devices.

Highly transparent, low sheet resistance and stable Tannic acid modified-SWCNT/AgNW double-layer conductive network for organic light emitting diodes

The fabrication of a carbon nanotube transparent conductive film by electrophoretic deposition and hot-pressing transfer

Ultrahigh-performance transparent conductive films of carbon-welded isolated single-wall carbon nanotubes

Fabrication and evaluation of adhesion enhanced flexible carbon nanotube transparent conducting films

Transparent Conducting Thin Film Preparation of Carbon Nanotube

Flexible White Organic Light-Emitting Diodes Based on Single-Walled Carbon Nanotube:Poly(3,4-Ethylenedioxythiophene)/Poly(Styrene Sulfonate) Transparent Conducting Film