STUDIES ON THE PREPARATION AND CURING REACTION KINETICS OF PHENOLIC RESIN/MONTMORILLONITE NANOCOMPOSITE
WB Xu,SP Bao,SJ Shen,SP Tang,PS He
DOI: https://doi.org/10.3321/j.issn:1000-3304.2002.04.011
2002-01-01
Abstract:The nanocomposite of phenolic resin/hexamethylenetetramine/montmorillonite, which was obtained by the treatment of inorganic montmorillonite, are prepared by casting and curing, and phenol resin exhibit crosslinked chains by chemical bonds-forming a three-dimensional network while the mechanisms of phenol resin are different. As a result, it has been investigated by X-ray diffraction (XRD) that the peak of 16-MMT(2theta = 4.02degrees) disappeared, and the first peak(n = 1) of montmorillonite at the resol phenol resin/16-MMT appeared at 2theta = 2.50 similar to 2.56degrees, while the diffraction peak of montmorillonite at the novolac resin/16-MMT has not easily been found. Thus, resol types of resin can form the intercalated nanocomposite with the lattice spacing of 3.53 similar to 3.45 nm, while novolac phenolic resin can partly form the exfoliated nanocomposite. The curing reaction of novolac phenolic resin has been studied by differential scanning calorimetry (DSC) at various heating rates. Some kinetics parameters including the reaction order and activation energy were calculated with Kissinger, Flynn-Wall-Ozawa and Crane methods. The curing kinetic of. novolac phenol resin gives information that activation energy and reaction order decrease with the addition of organic montmorillonite. The value of E obtained for the neat novolac resin was 162.3 kJ/mol, and those of the systems with 5, 7 and 10 percents of organic montmorillonite were 139.2, 142.8 and 122.6 kJ/mol respectively. It was observed that the reaction order of the pure system was 1.13, and the systems with 5,7 and 10 percents of organic montmorillonite. were 0.95, 0.92, 0.95. With the reduction of the activation energy and the raction order,it is possible to take advantage to the application of nanocomposite.