Effect of 0.770wt%h Addition on the Microstructure of Ti–6Al–4V Alloy and Mechanism of Δ Hydride Formation

Tangkui Zhu,Miaoquan Li
DOI: https://doi.org/10.1016/j.jallcom.2009.03.019
IF: 6.2
2009-01-01
Journal of Alloys and Compounds
Abstract:Ti–6Al–4V alloy was hydrogenated at 750°C below the eutectoid transformation temperature with 0.770wt%H, and its microstructural evolution and phase transformations were investigated by the use of optical microscopy (OM), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results show that, in comparison to the as-received alloy, the contrasts of equiaxed α phase and transformed β phase under optical microscope in the hydrogenated one were reversed. The XRD peaks of β phase after hydrogenation moved to lower angles obviously because of the lattice expansion of β phase with the solution of hydrogen atoms, and the XRD peaks of α phase were broadened due to microscopic internal stress. In addition, XRD and TEM analysis revealed that the face-centered cubic (FCC) δ hydride could precipitate not only in α phase but also in β phase. Furthermore, the mechanisms of δ hydride formation were discussed, and the results showed that the hydrogen diffusion has a significant effect on the δ hydride formation.
What problem does this paper attempt to address?