Abstract:In this paper, porous zinc oxide (ZnO) nanosheets were successfully prepared by a simple low-temperature hydrothermal method. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Brunauer–Emmett–Teller (BET) tests showed that the synthesized product was ZnO with porous sheet structure. The diameter of porous nanosheets was about 100 nm and the thickness was about 8 nm. As a photocatalyst, the degradation efficiencies of porous ZnO nanosheets for methyl orange (MO), methylene blue (MB) and Rhodamine B (RhB) were 97.5%, 99% and 96.8%, respectively. In addition, the degradation efficiency of ZnO for mixed dyes (Mo, MB and RhB) was satisfactory, reaching 97.7%. The photocatalytic stability of MB was further tested and remained at 99% after 20 cycles. In the experiment, ZnO/FTO (fluorine-doped tin oxide) composites were prepared by using ZnO as the conductive layer. Titanium dioxide (TiO2) was deposited on the surface of ZnO/FTO by electrodeposition, so as to obtain a TiO2/ZnO/FTO composite. By studying the electrochromic properties of this composite, it was found that the TiO2/ZnO/FTO composite shows a large light modulation range (55% at 1000 nm) and excellent cycle stability (96.6% at 200 cycles). The main reason for the excellent electrochromic properties may be the synergistic effect between the porous structure and the polymetallic oxides. This study is helpful to improve the photocatalytic efficiency and cycling stability of metal oxides, improve the transmittance of thin films and provide a new strategy for the preparation of ZnO composite materials with excellent photocatalytic and electrochromic properties.

Synthesis of ZnO/TiO2 nanotube composite film by a two-step route

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Effect of ZnS Layers on Optical Properties of Prepared CdS/TiO2 Nanotube Arrays for Photocatalyst

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Zinc-Doped TiO<sub>2</sub> Nanotube Arrays

Fabrication and Photocatalytic Properties of TiO_2-ZnO Nano-composite Material

Two-step anodization fabrication of ordered ZrO2 nanotube arrays

One-Step Fabrication of Cds Nanoparticle-Sensitized Tio2 Nanotube Arrays Via Electrodeposition

Anodization Fabrication of Highly Ordered Tio2 Nanotubes

Synthesis of the Porous ZnO Nanosheets and TiO2/ZnO/FTO Composite Films by a Low-Temperature Hydrothermal Method and Their Applications in Photocatalysis and Electrochromism

Synthesis and Photoinduced Charge-Transfer Properties of a ZnFe2O4-sensitized TiO2 Nanotube Array Electrode.

Synthesis of zinc oxide nanorods using carbon nanotubes as templates

Tube-In-Tube Tio2 Nanotubes with Porous Walls: Fabrication, Formation Mechanism, and Photocatalytic Properties

Nanotubular ZrTiO 4 Prepared on Sputter Deposited Zr−Ti Films by Anodization

Fabrication of Titanium Oxide Nanotube Arrays by Anodic Oxidation

Fabrication of Tubular ZnO by Vesicle–template Fusion

Electrochemical Method for Synthesis of a ZnFe2O4/TiO2 Composite Nanotube Array Modified Electrode with Enhanced Photoelectrochemical Activity

Fabricating Gold Nanoparticle-Oxide Nanotube Composite Materials by a Self-Assembly Method.

From Single-Component Nanowires to Composite Nanotubes

Fabrication and microstructure analysis on zinc oxide nanotubes

Synthesis of TiO<sub>2</sub> Nanotube Arrays Through Multistep Anodization