Abstract:Highly ordered TiO2 nanotube array electrodes were successfully fabricated by a two-step anodization method on Ti sheet substrates in an electrolyte composed of ammonium fluoride, deionized water, and glycol. The tube wall was smooth, and the average internal and external diameters, wall thickness, and tube length achieved were 80 nm, 90 nm, 10 nm, and 9 μm, respectively. X-ray diffraction and field emission scanning electron microscopy results revealed that the TiO2 nanotube arrays presented an amorphous structure. When calcined at 300 °C, the arrays crystallized into the anatase phase, and the crystallization degree of the oxide layer increased as the temperature rose. Calcinating at 400 °C did not obviously disrupt the porous structure of the highly ordered arrays. However, higher temperature enlarged the diameter of the nanotube array and roughened the tube wall. When the temperature reached 600 °C, the nanotube mouth broke because of the excessive stress, causing the oxide layer’s thinness and nanotube mouth clogging. The photoelectric test showed that the electrode presented obvious photoresponse under 300–400 nm UV excitation (maximized at 360 nm). The degree of crystallization and the micro-structure of the oxide layer can significantly affect the photoelectric properties of the electrode. After calcination at 400 °C, the TiO2 nanotube arrays, with highly ordered tubular structure directly connected to the Ti substrate, can ensure the rapid transportation of photo-induced electrons to the Ti substrate, while the high crystallinity of the arrays can help reduce the defect density of the nanotube and extend the lifetime of the photo-induced carriers. The electrode showed the best photoelectric property, and the photocurrent intensity was maximized (29.6 μA). However, the calcination process with over-temperature resulted in substantial loss of the TiO2 oxide layer, mouth clogging, and a severe decline in the photoelectric properties.

Zinc-Doped TiO<sub>2</sub> Nanotube Arrays

Effect of ZnS Layers on Optical Properties of Prepared CdS/TiO2 Nanotube Arrays for Photocatalyst

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Temperature-dependent differences in wettability and photocatalysis of TiO 2 nanotube arrays thin films

One-Step Fabrication of Cds Nanoparticle-Sensitized Tio2 Nanotube Arrays Via Electrodeposition

Synthesis of ZnO/TiO2 nanotube composite film by a two-step route

Synthesis and Photoinduced Charge-Transfer Properties of a ZnFe2O4-sensitized TiO2 Nanotube Array Electrode.

Tube-In-Tube Tio2 Nanotubes with Porous Walls: Fabrication, Formation Mechanism, and Photocatalytic Properties

Boron-doped TiO2 Nanotube Array: in Situ Electrochemical Preparation and Study on Its Photocatalytic Activity

Nitrogen-Doped TiO<sub><b>2</b></sub>Nanotube Arrays with Enhanced Photoelectrochemical Property

TiO<sub>2</sub> Nanowires/Nanobelts Originating from Anodically Grown Nanotube Arrays

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.

Zero-valent Nanophase Iron and Nitrogen Co-Modified Titania Nanotube Arrays: Synthesis, Characterization, and Enhanced Visible-Light Photocatalytic Performance

Nitrogen-Doped Tio2 Nanotube Arrays With Enhanced Photoelectrochemical Property

Fabrication of Cu2o/Tio2 Nanotube Heterojunction Arrays and Investigation of Its Photoelectrochemical Behavior

Facile synthesis and enhanced visible light photocatalytic activity of N and Zr co-doped TiO2 nanostructures from nanotubular titanic acid precursors

Synthesis of zinc oxide nanorods using carbon nanotubes as templates

Fabrication and microstructure analysis on zinc oxide nanotubes

Fabrication of Highly-Oriented TiO2 Nanotube Arrays and Its Application in Dye-Sensitized Solar Cells

Preparation and Doping of Anodic Tio2 Nanotube Array

Morphology of TiO_2 Nanotube Arrays Prepared by Anodic Oxidation

Zinc-Doped TiO&lt;sub&gt;2&lt;/sub&gt; Nanotube Arrays