Abstract:Because of the high specific surface area and enhanced charge migration, TiO2 with unique belt-like nanostructures finds promising applications in various fields such as photocatalysis, dye-sensitized solar cells, gas sensors, and Li-ion batteries. In the current study, a solution combustion procedure was firstly adopted to prepare a black water-proof precursor. The black precursor interacted with H2O2 at ambient temperature, achieving a precursor solution that is capable of fabricating hydrogen titanate (H2Ti2O5·H2O) nanobelt arrays on metallic Ti substrates at 60 °C. Subsequent calcination in air at 400 °C achieved arrays of ultrathin anatase TiO2 nanobelts of ca. 2–4 nm in thickness. The addition of nickel nitrate in the combustion solution achieved the Ni-doping into the resultant TiO2 nanobelts, which did not alter the nanobelt structure but significantly reduced the band gap from 3.2 eV to 2.9 eV. When compared with the commonly alkali-hydrothermal synthesized anatase TiO2 nanobelts, the present ultrathin nanobelts exhibited much improved photocatalytic activity when utilized to assist photodegradation of rhodamine B in water. The ultrathin nanobelt structure is believed to contribute to the high specific surface area, the much reduced charge migration path, and the enhanced charge transport along the longitudinal direction. The appropriate Ni-doping further enhanced the photocatalytic performance, because of the increased light harvesting efficiency and reduced charge recombination.

Facile synthesis and enhanced visible light photocatalytic activity of N and Zr co-doped TiO2 nanostructures from nanotubular titanic acid precursors

Facile Fabrication of N-doped TiO2 Nanocatalyst with Superior Performance under Visible Light Irradiation

Effect of ZnS Layers on Optical Properties of Prepared CdS/TiO2 Nanotube Arrays for Photocatalyst

Facile Synthesis of Ni-doped TiO2ultrathin Nanobelt Arrays with Enhanced Photocatalytic Performance

Synthesis and Photoelectrochemical Studies of N, Zr Co-Doped Mesoporous Titanium Dioxide

Preparation, characterization and photocatalytic activity of N-doped NaTaO3 nanocubes

The Fabrication and Characterization of Novel Carbon Doped TiO2nanotubes, Nanowires and Nanorods with High Visible Light Photocatalytic Activity

Facile Synthesis of Mn-doped TiO2 Nanotubes with Enhanced Visible Light Photocatalytic Activity

Facile Synthesis of Anatase–Rutile Diphase N-doped TiO2 Nanoparticles with Excellent Visible Light Photocatalytic Activity

Enhancement of Visible-Light-Induced Photocurrent and Photocatalytic Activity of V and N Codoped TiO2 Nanotube Array Films

Nitrogen-Doped Tio2 Nanotubes with Enhanced Photocatalytic Activity Synthesized by A Facile Wet Chemistry Method

Carbon Coated N-Doping of TiO2 Nanotube Films with Enhanced Visible-Light Photocatalytic Activity

Synthesis, Characterization and Photocatalytic Activity of Visible-light-driven N-P-codoped TiO_2 Nanotubes

Zero-valent Nanophase Iron and Nitrogen Co-Modified Titania Nanotube Arrays: Synthesis, Characterization, and Enhanced Visible-Light Photocatalytic Performance

Synthesis of Novel, Visible-Light Driven S,N-doped NaTaO3 Catalysts with High Photocatalytic Activity

Efficient Fabrication of ZrO2-doped TiO2 Hollow Nanospheres with Enhanced Photocatalytic Activity of Rhodamine B Degradation.

Carbon-Doped ZnO Nanostructures: Facile Synthesis and Visible Light Photocatalytic Applications

Improving the thermal stability and photocatalytic activity of nanosized titanium dioxide via La3+ and N co-doping

Preparation, Photocatalytic Activity, and Mechanism of Nano-Tio2 Co-Doped with Nitrogen and Iron (Iii)