The microstructure and magnetic properties of NdFeB magnets directly solidified at a low cooling rate

Zongjun Tian,Shandong Li,Kun Peng,Benxi Gu,Jianrong Zhang,Mu Lu,Youwei Du

DOI: https://doi.org/10.1016/j.msea.2004.03.077

2004-01-01

Abstract:Nd12.5Fe82B5.5 ribbons have been prepared by a melt spinning technique at a wheel speed ranging from 5 to 22m/s. It was found that the wheel speed vR dramatically influences the microstructure and magnetic properties of the ribbons. At an optimized vR, a structure with single-phase Nd2Fe14B and an enhanced coupling between grains give rise to excellent magnetic properties. For example, the coercivity, remanence ratio, and maximum energy product of the best sample quenched at a wheel speed of 13m/s are 1227.4kA/m, 0.76, and 182.6kJ/m3, respectively. In comparison with the samples from under- and over-quenched conditions and all the samples with annealing, the as-quenched sample fabricated at the optimized wheel speed has the best magnetic properties.