Abstract:Carbothermal reduction-nitridation method is an effective means for synthesizing Si3N4 powder. Herein, spherical monodisperse silica was used as silicon source. The effects of reaction temperature, nitrogen flow rate and Si3N4 seeds content on the products were studied. It was found that high-purity α-Si3N4 (>99.0 wt%) was synthesized from C/SiO2 = 3:1 at 1400 °C, reaction time of 6 h and nitrogen flow rate of 800 ml/min. The powder, with an average size of 0.5 μm, showed good dispersity and regular morphology because spherical monodisperse silica could be completely coated with carbon. The more contact sites between SiO2 and C, the higher concentration of SiO(g) would be produced in the initial stage. It also indicated that the nucleation rate of α-Si3N4 increased, thereby inhibiting the formation of an agglomerate phase and suppressing the grain growth of α-Si3N4. Furthermore, higher nitriding temperature and Si3N4 seeds content both decreased the grain size and increased β-Si3N4 content. The forming mechanism of non-agglomerated and submicron-sized α-Si3N4 was clarified.

Solvothermal Synthesis of Si3n4 Nanomaterials at A Low Temperature

Additive‐Assisted Nitridation to Synthesize Si3N4 Nanomaterials at a Low Temperature

Additive-Assisted Nitridation to Synthesize Si<sub>3</sub>N<sub>4</sub>Nanomaterials at a Low Temperature

Low‐Temperature Synthesis of Nanocrystalline Α‐si3n4 Powders by the Reaction of Mg2Si with NH4Cl

Sulfur-assisted Fabrication of Silicon Nitride Nanorods in Autoclaves at 250 °C

Low-Temperature Synthesis of Nanocrystalline α-Si<sub>3</sub>N<sub>4</sub>Powders by the Reaction of Mg<sub>2</sub>Si with NH<sub>4</sub>Cl

Low temperature synthesis of SiCN nanostructures

Large-scale synthesis of magnenium silicon nitride powders at low temperature

Synthesis of monodisperse and high-purity α-Si3N4 powder by carbothermal reduction and nitridation

Solid State Synthesis of Nitride, Carbide and Boride Nanocrystals in an Autoclave

Synthesis and characterization of nanocrystalline NiSb and NiSb2 at low temperature

Synthesis of Α Silicon Nitride Single-Crystalline Nanowires by Nitriding Cryomilled Nanocrystalline Silicon Powder

Synthesis of Si 3 N 4 Nanowires by Catalyst‐free Nitridation of (si + SiO 2 ) Mixture

Synthesis of Si 3 N 4 powder with tunable α/β-Si 3 N 4 content from waste silica fume using carbothermal reduction nitridation

A simple method to synthesize Si3N4 and SiO2 nanowires from Si or Si/SiO2 mixture

Yttrium Oxide-Assisted Crn Synthesis of Silicon Oxynitride Powders with Controlled Morphology

Silicon nano-wires grown at low temperature

Solution-phase Synthesis of Nanomaterials at Low Temperature

Growth Of Sic Nanorods At Low Temperature

Low Temperature Solid-State Synthesis of Nanocrystalline Gallium Nitride

Direct Synthesis of Α-Silicon Nitride Nanowires from Silicon Monoxide on Alumina