Abstract:Exploring the temperature-dependent photoluminescence (PL) properties of quantum dots (QDs) is not only important for understanding the carrier recombination processes in QD-based devices but also critical for expanding their special applications at different temperatures. However, there is still no clear understanding of the optical properties of CdS/ZnS core/shell QDs as a function of temperature. Herein, the temperature-dependent PL spectra of CdS/ZnS core/shell QDs were studied in the temperature range of 77–297 K. It was found that the band-edge emission (BEE) intensity decreases continuously with increasing temperature, while the surface-state emission (SSE) intensity first increases and then decreases. For BEE intensity, in the low temperature range, a small activation energy (29.5 meV) in the nonradiative recombination process led to the decrease of PL intensity of CdS/ZnS core/shell QDs; and at high temperature the PL intensity attenuation was caused by the thermal escape process. On the other hand, the temperature-dependent variation trend of the SSE intensity was determined by the competition of the trapping process of the surface trap states and the effect of thermally activated non-radiative defects. As the temperature increased, the PL spectra showed a certain degree of redshift in the peak energies of both band-edge and surface states and the PL spectrum full width at half-maximum (FWHM) increases, which was mainly due to the coupling of exciton and acoustic phonon. Furthermore, the CIE chromaticity coordinates turned from (0.190, 0.102) to (0.302, 0.194), which changed dramatically with temperature. The results indicated that the CdS/ZnS core/shell QDs are expected to be applied in temperature sensors.

Temperature Dependence of Photoluminescence from Self-Organized Ge Quantum Dots with Large Size and Low Density

Photoluminescence Lifetime and Absorption Spectrum of Pbs Nanocrystal Quantum Dots

Structure and Photoluminescence of Ge Nanoparticles Embedded in SiO2 Gel Glasses Fabricated at Different Temperatures

Systematic Studies of the Photoluminescence of Ge Quantum Dots Grown on Strained Si(0.7)Ge(0.3) Buffer Layer

Optical properties of Ge/Si quantum dot superlattices

Photoluminescence from Colloidal CdS-CdSe-CdS Quantum Wells

PHOTOLUMINESCENCE STUDY OF MULTILAYER in In_(0.55)Al_(0.45)As/A_(0.5)Ga_(0.5)As QUANTUM DOT AT VARIOUS TEMPERATURE

Thermal Quenching Of Luminescence From Buried And Surface Ingaas Self-Assembled Quantum Dots With High Sheet Density

Temperature-dependent Photoluminescence of Highly Luminescent Water-Soluble CdTe Quantum Dots

Temperature-Dependent Photoluminescence of CdS/ZnS Core/Shell Quantum Dots for Temperature Sensors

Exciton Radiative Recombination in Spherical CdS∕CdSe∕CdS Quantum-Well Nanostructures

Temperature-Enhanced Exciton Emission from GaAs Cone-Shell Quantum Dots

Temperature behavior of excitation emission in self-organized InAs quantum dots

Temperature-dependent photoluminescence: A theoretical study

Temperature Dependence of Exciton Localization in ZnO/Zn1−xMgxO Multiple Quantum Wells with Different Barrier Compositions

Influence of Size and Surface State Emission on Photoluminescence of CdSe Quantum Dots under UV Irradiation

Mid-Infrared Photoluminescence of Pbse/Pbsrse Multiple Quantum Wells Grown by Molecular Beam Epitaxy

Dependence of Photoluminescence of ZnO/Zn0.85Mg0.15O Multi-Quantum Wells on Barrier Width

Temperature-Dependent Luminescence Originating from the Recombination of Excitons in Organic Light-Emitting Materials

Anomalous Temperature Dependence of Photoluminescence Caused by Non-Equilibrium Distributed Carriers in InGaN/(In)GaN Multiple Quantum Wells