Abstract:The hydration exothermic rate of fly ash concrete is significantly affected by the initial concreting temperature and water-binder ratio. Firstly, the adiabatic temperature rise and temperature rise rate of fly ash concrete at different initial concreting temperatures and water-binder ratios were obtained by a thermal test instrument; then, the effects of initial concreting temperature and water-binder ratio on the hydration kinetic parameters of the NG-I-D hydration process of fly ash concrete were analyzed by the theory of hydration kinetics; lastly, the effects of initial concreting temperature and water-binder ratio on chemically bound water and pore bulk of fly ash concrete during hydration were analyzed by applying a thermogravimetric analyzer and industrial CT scanning techniques. The results showed that the increase in initial concreting temperature and the decrease in water-binder ratio accelerated the rate of temperature rise, and the initial concreting temperature had a more significant effect than the water-binder ratio. During the hydration reaction, the I process was significantly influenced by the initial concreting temperature, and the D process was significantly influenced by the water-binder ratio; the content of bound water increased with the increase in water-binder ratio and age and the decrease in initial concreting temperature. The initial temperature had a significant effect on the growth rate of 1 to 3 days bound water, and the water-binder ratio had a more significant effect on the growth rate of 3 to 7 days bound water. The porosity was positively correlated with the initial concreting temperature and water-binder ratio and decreased with age, but 1 to 3 days was the key period of porosity change. Additionally, the pore size was also influenced by the initial concreting temperature and water-binder ratio.

The influence of W/B ratio and fly ash addition on the autogenous shrinkage of concrete with same strength

The Influence of Fly Ash Addition on the Autogenous Shrinkage of High-Strength Concrete

Influence of Mineral Admixtures on early Shrinkage of Ordinary Concrete

Study on the Effect of Fly Ash and Polycarboxylic Acid Water Reducer on the Properties of Recycled Concrete

Autogenous Shrinkage Measuring of Concrete and Model Analysis

Influences of Water-binder Ratio and Dosage of Fly Ash on Autogeneous Shrinkage of Shrinkage-Compensating Concrete

THE AUTOGENOUS SHRINKAGE OF CONCRETES PREPARED WITH THE BINDERS CONTAINING DIFFERENT KINDS OF MINERAL ADMIXTURE

Early-age Shrinkage Behavior of Cement-Fly Ash Paste under Wind Speeds: A Study Using BSE-IA and MIP Techniques

Influence of Shrinkage Retarder on Early Self-Shrinking of Concrete

Experimental Study on the Cracking Resistance at Early Ages of High Performance Concrete Added with Lithium Slag and Fly Ash

Influence Mechanism of Initial Concreting Temperature and Water-Binder Ratio on Hydration Rate of Fly Ash Concrete

Experimental Analysis of Adiabatic Temperature Rise of Fly Ash Concrete

Influence of Fly Ash on the Deformation of Shrinkage-compensating Concrete with the Same Level of Strength

Influence of expansive agent on the cracking resistance performance of fly ash concrete

Influence of Superplasticizer and Shrinkage-Reducing Admixtures on Early Age Shrinkage of Concrete

Design and Control Shrinkage Behavior of High-Strength Self-Consolidating Concrete Using Shrinkage-Reducing Admixture and Super-Absorbent Polymer

Internal Curing Efficiency of Prewetted LWFAs on Concrete Humidity and Autogenous Shrinkage Development

Effect of fly ash on shrinkage of self-compacting concrete using restrained ring test

Integrative Study on the Effect of Internal Curing on Autogenous and Drying Shrinkage of High-Strength Concrete

Influence of water to binder ratio and content on fly ash activity factor

Influence of Water-Binder Ratio and Fly Ash on the Adiabatic Temperature Rise of Concrete