Abstract:Fly ash has been widely used as supplementary cementitious material in concrete industry. Hydration mechanism of composite binder containing fly ash is much more complicated due to the mutual effect of the hydration of cement and the pozzolanic reaction of fly ash. This paper involves the hydration kinetics of composite binder containing up to 65 % of fly ash and comparison of the results with data on composite binder containing slag that are previously published. The hydration heat evolution rate and cumulative hydration heat of composite binder containing fly ash were measured at 298, 318 and 333 K with an isothermal calorimeter. Based on the hydration kinetics model, three hydration processes, namely nucleation and crystal growth (NG), interactions at phase boundaries (I) and diffusion (D) were characterized, the relationship between the hydration rate and hydration degree was discussed at different stages, and kinetics parameters, n, K and Ea, were calculated and analyzed. Results show that the hydration heat evolution rate and cumulative hydration heat of composite binder obviously decrease with increasing the replacement ratio of fly ash. Elevated temperatures promote the hydration process, especially for composite binder containing high amount of fly ash. The kinetics model could simulate the hydration process of composite binder containing no more than 65 % of fly ash, whose hydration process sequence is NG → I → D at 298 and 318 K, but it becomes NG → D at 333 K. Fly ash has relatively smaller effect on the overall reaction of composite binder than slag. The reaction rates of composite binder containing fly ash at different stages are higher than those of composite binder containing slag at the same replacement ratio. The value of Ea for the overall reaction of composite binder decreases first and then increases with increasing the content of fly ash, and it is lower than that of composite binder containing slag at the same replacement ratio.

Influence Mechanism of Initial Concreting Temperature and Water-Binder Ratio on Hydration Rate of Fly Ash Concrete

Influence of Initial Casting Temperature and Dosage of Fly Ash on Hydration Heat Evolution of Concrete under Adiabatic Condition

Influence of Mineral Admixtures on early Shrinkage of Ordinary Concrete

Experimental Analysis of Adiabatic Temperature Rise of Fly Ash Concrete

Influence of Water-Binder Ratio and Fly Ash on the Adiabatic Temperature Rise of Concrete

Effect of Thermal Environment at Early Age on Hydration Phases Composition and Strength Development of Concrete Containing Fly Ash

The Influential Factors of Adiabatic Temperature Rise of Concrete

Research on Hydration Degree of Cement-Fly Ash Complex Binders

Performance of concrete containing fly ash at early ages

Effect of Water-to-binder Ratio on the Hydration Kinetics of Composite Binder Containing Slag or Fly Ash

Influence of Mineral Admixture on Early-Age Concrete Cracking

Hydration Kinetics of Composite Binder Containing Slag at Different Temperatures

Mechanism of fly ash's effects during hydration process of composite binder

Contributions of Fly Ash and Ground Granulated Blast-Furnace Slag to the Early Hydration Heat of Composite Binder at Different Curing Temperatures

Influence of Fly Ash on the Compressive Strength of Concrete under Temperature Match Curing Conditions

Experiment and Analysis of Concrete Adiabatic Temperature Rise

Effects of Mixing and Curing Temperature on the Strength Development and Pore Structure of Fly Ash Blended Mass Concrete

Effects of ultrafine fly ash on the properties of high-strength concrete

Strength Development And Thermogravimetric Investigation Of High-Volume Fly Ash Binders

Influence of water to binder ratio and content on fly ash activity factor

The Influence of Ground Fly Ash on Cement Hydration and Mechanical Property of Mortar